对第二代DD6单晶高温合金进行了标准热处理和热等静压处理＋标准热处理,然后再在850℃和300~850 MPa应力条件下进行高温高周疲劳试验,观察了不同处理状态合金的显微组织,分析了热等静压处理对合金显微组织和高温高周疲劳性能的影响.结果表明：与仅进行标准热处理的合金相比,增加热等静压处理后,合金内部显微疏松的数量和尺寸显著降低,其体积分数从0．31％降低到0．04％,合金的高周疲劳强度由331 MPa提高至433 MPa,高周疲劳寿命也显著提高.
Standard heat treatment and hot isostatic pressing(HIP)followed by standard heat treatment were conducted on a second generation single crystalsuperalloy DD6,and then high-temperature high cycle fatigue (HCF) test were carried out under the conditions of 850 ℃ and stress between 300 MPa and 850 MPa.The microstructure of the alloy in different states was observed,and the effects of HIP on microstructure and HCF properties of the alloy were investigated.The results show that,compared with the alloy only treated with standard heat treatment, the number and size of porosity in the alloy treated by HIP decreased obviously,the volume fraction of porosity deceased from 0.31% to 0.04%;its high cycle fatigue strengths increased from 331 MPa to 433 MPa,and its high cycle fatigue life raised sharply.
参考文献
| [1] | 杨素玲;郑运荣.电厂燃气涡轮用单晶高温合金的进展[J].机械工程材料,2002(4):6-10. |
| [2] | 陈柏凡;李辉.一种第二代镍基单晶高温合金固溶时效处理工艺的确定[J].机械工程材料,2013(5):18-21,25. |
| [3] | Stanislaw Roskosz;Janusz Adamiec.Methodology of quantitative evaluation of porosity, dendrite arm spacing and grain size in directionally solidified blades made of CMSX-6 nickel alloy[J].Materials Characterization,200910(10):1120-1126. |
| [4] | 呼和.镍基铸造高温合金的热等静压处理[J].金属学报,2002(11):1199-1202. |
| [5] | 张剑;赵云松;贾玉亮;杨帅;骆宇时;唐定中.一种镍基单晶高温合金的热机械疲劳行为[J].机械工程材料,2013(8):41-44,49. |
| [6] | Q. Z. Chen;Y. H. Kong;C. N. Jones;D. M. Knowles.Porosity reduction by minor additions in RR2086 superalloy[J].Scripta materialia,20042(2):155-160. |
| [7] | 赵云松;张剑;骆宇时;唐定中;冯强.Hf对第二代镍基单晶高温合金DD11高温低应力持久性能的影响[J].金属学报,2015(10):1261-1272. |
| [8] | 赵乃仁;金涛;孙晓峰;管恒荣;杨洪才;胡壮麒.抽拉速率对SRR99单晶高温合金组织和性能的影响[J].材料研究学报,2008(1):46-52. |
| [9] | H.V. ATKINSON;S. DAVIES.Fundamental Aspects of Hot Isostatic Pressing: An Overview[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,200012(12):2981-3000. |
| [10] | 韩梅;骆宇时.热等静压对DD3单晶高温合金组织与性能的影响[J].材料工程,2008(8):40-43. |
| [11] | Epishin, A.;Fedelich, B.;Link, T.;Feldmann, T.;Svetlov, I.L..Pore annihilation in a single-crystal nickel-base superalloy during hot isostatic pressing: Experiment and modelling[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2013:342-349. |
| [12] | Zhenxue Shi;Xiaoguang Wang;Shizhong Liu;Jiarong Li.Low cycle fatigue properties and microstructure evolution at 760 ℃ of a single crystal superalloy[J].自然科学进展（英文版）,2015(01):78-83. |
| [13] | 韩国明;张振兴;李金国;金涛;孙晓峰;胡壮麒.DD98M镍基单晶高温合金900℃高周疲劳行为[J].金属学报,2012(2):170-175. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%