某油田用闸板防喷器的40CrNiMo钢剪切闸板在使用过程中发生了刃口断裂事故，为找到刃口断裂的原因，对其进行了断口形貌观察、显微组织分析、化学成分分析、力学性能测试等。结果表明：40CrNiMo钢剪切闸板刃口在较大冲击力作用下发生了脆性断裂；断裂是因钢的韧性不足、晶界间的夹杂物颗粒等导致裂纹萌生和扩展；刃口断裂的主要原因是40CrNiMo钢在调质热处理过程中的回火温度偏低或保温时间过短。
In an oil field,the edge of 40CrNiMo steel shear ram of blow-out preventer cracked.In order to find the fracture reasons of the ram edge,fracture morphology observation,microstructure analysis,chemical composition analysis,mechanical properties testing were used to analyze the fracture.The results indicate that,for 40CrNiMo steel ram edge,brittle fracture occurred under the role of greater impact force;The occurrence and propagation of cracks were caused by lack of ductility and inclusions particles at the grain boundaries of 40CrNiMo steel.The main reasons of edge fracture were lower tempering temperature or shorter holding time during the process of quenching and tempering heat treatment.
参考文献
| [1] | 陈惠琴;唐波;何为.闸板防喷器密封失效原因及对策分析[J].天然气工业,2006(11):80-82. |
| [2] | 唐洋;耿海涛;钟林;邓长飞;李军刚.闸板防喷器密封原理与失效分析[J].润滑与密封,2013(2):91-94. |
| [3] | 张耀明.剪切闸板在井喷失控抢险中的成功运用[J].钻采工艺,2001(01):66-67,71. |
| [4] | 王锡洲;付玉坤;朱海燕;韩传军.闸板防喷器胶芯密封及损坏机理分析[J].石油矿场机械,2010(2):16-18. |
| [5] | 刘智勇;翟国丽;董超芳;李晓刚;孟庆昆.40CrNiMo钻杆钎头失效分析[J].物理测试,2007(5):53-58. |
| [6] | 孙维连;杨钰瑛.35CrMo钢拉杆显微组织与性能[J].金属热处理,2005(11):79-82. |
| [7] | 龚丹梅;袁鹏斌;余世杰;何卫滨.S135钢级钻杆管体断裂原因分析[J].金属热处理,2013(7):118-121. |
| [8] | 傅志强,潘宏伟,陈广志,王建,孟凯,侯书健.40CrNiMo钢齿轮轴断裂原因分析[C].2011年全国失效分析学术会议论文集,2011:376-378. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%