抗拉强度780 MPa级冷成型用热连轧高强钢在工程起重机和混凝土泵车上得到了广泛使用。为进一步改善此种高强钢的力学性能与使用性能，对其热轧卷开平后的横切钢板在热连轧带钢热处理线进行回火热处理。对回火钢板的力学性能、焊接性能、压型性能和显微组织进行检验与分析。结果表明：热轧钢板经回火热处理后，钢板强度和硬度有明显提高，冲击韧性与伸长率略有降低，横向与纵向力学性能差异减小；焊后失强率降低，焊接接头力学性能得到改善；压型性能得到极大改善。在微观结构上，回火后钢板的组织类型无显著改变，但部分铁素体晶粒长大、粗化，回火后铁素体中位错密度降低，近等轴位错胞状结构增多，而固溶Ti、Nb、Mo元素以（Ti,Nb,Mo）C形式继续析出，产生沉淀硬化。
Leveled steel plates were taken from hot-rolled strip steel with tensile strength of 780 MPa, which had been widely used in building cranes and concrete pump trucks by cold forming. In the present work, the plates were tem-pered on a production line, and their mechanical properties, welding performance, cold forming property and microstruc-tures were investigated. The results show that the strength and hardness of the steel increased significantly after the temper-ing, while the impact toughness and elongation rate decreased slightly. The difference between the mechanical properties in transverse direction and these in longitudinal direction decreased due to the tempering. The mechanical properties of the welded joints were improved showing reduced strength-loss after welding. The cold forming performance was also greatly improved. No significant change in phase constituents was observed due to the tempering, however, some ferrites grains were coarsened and their dislocation density decreased associated with increasing of cellular dislocation. Increased precipi-tates containing Ti, Nb, Mo were observed, resulting in the precipitation hardening.
参考文献
| [1] | Naoki N;Matthias M .Modeling of Microstructure Evolution During Hot Rolling of a 780 MPa High Strength Steel[J].ISIJ International,2005,45(01):82. |
| [2] | 王晓南,杜林秀,张海仑,邸洪双.780MPa级重载汽车用大梁钢的工业试制[J].钢铁研究学报,2011(05):45-49. |
| [3] | 王晓南,邸洪双,杜林秀.形变及冷却速率对热轧超高强汽车钢板中纳米析出的影响[J].金属学报,2012(05):621-628. |
| [4] | 赵培林,孙新军,杜显彬,王建军,雍岐龙.终冷温度对不同成分700MPa级耐候钢组织和性能的影响[J].金属热处理,2011(06):87-91. |
| [5] | J. H. Jang;Y.-U. Heo;C.-H. Lee .Interphase precipitation in Ti-Nb and Ti-Nb- Mo bearing steel[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2013(3):309-313. |
| [6] | Misra RDK;Nathani H;Hartmann JE;Siciliano F .Microstructural evolution in a new 770 MPa hot rolled Nb-Ti microalloyed steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):339-352. |
| [7] | Funakawa Y;Shiozaki T;Tomita K;Yamamoto T;Maeda E .Development of high strength hot-rolled sheet steel consisting of ferrite and nanometer-sized carbides[J].ISIJ International,2004(11):1945-1951. |
| [8] | Kagechika H .Recent Progress and Future Trends in the Re-search and Development of Steel[J].NKK Technical Review,2003,88:6. |
| [9] | 黄庆渊;颜鸿威;潘永村 等.纳米级析出物强化热轧汽汽车用钢开发[J].矿冶,2010,53(04):45. |
| [10] | 李杏娥,赵志毅,薛润东,杨晓臻,谢建新.Ti在热轧高强带钢中的析出相与性能关系的研究[J].钢铁,2008(06):70-73. |
| [11] | 赵培林,孙新军,汤化胜,段明波,雍岐龙.热轧高强带钢同卷强度波动原因探讨及分析[J].钢铁,2011(08):56-62. |
| [12] | Weng Y Q;Dong H;Gan Y.Advanced Steels:The Recent Sce-nario in Steel Science and Technology[M].Beijing:Metallurgi-cal Industry Press,2011:317. |
| [13] | 康军艳,余伟,陈银莉.回火工艺对针状铁素体钢组织和性能的影响[J].钢铁,2006(09):65-69. |
| [14] | 白晓虹,刘东升.屈服强度700 MPa级冷成形用热轧带钢的开发[J].钢铁,2013(07):76-83. |
| [15] | 李国宝.X60管线钢回火工艺对力学性能的影响[J].宽厚板,2007(04):31-33. |
| [16] | Bracke L;Wispelaere N D;Ahmed H et al.S700MC/Grade 100 in Heavy Gauges:Industrialisation at Arcelor Mittal Europe[J].Revue de Métallurgie,2011,108:323. |
| [17] | Suikkanen P .Development and Processing of Low Carbon Bainitic Steels[D].Linnanmaa:University of Oulu,2009. |
| [18] | 雍岐龙.钢铁材料中的第二相[M].北京:冶金工业出版社,2006 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%