为了揭示0.1%C-5%Mn钢的板坯内部裂纹的产生机理，采用物理测试、金相分析和设计热模拟试验等方法，研究了不同冷却模式下钢的组织及裂纹特征。结果表明，高的冷却强度下铸坯内部出现了大量的马氏体和裂纹，冷却强度越大马氏体相越多，裂纹宽度越大。采用缓冷或热送的工艺能够防止快速冷却引起的马氏体相变，形成粒状贝氏体组织，由此可以控制内部裂纹的产生和扩展。
In order to reveal formation mechanism of slab internal crack of the 0.1%C-5%Mn steel,structure and crack feature of this steel have been researched under different cooling models by using methods such as physical test,metallo-graphic examination etc and designing heat simulation experiment. The results show that a lot of martensite and crack ap-peared in the slab when the cooling intensity was high.The higher the cooling intensity,the more martensite phase had and the greater the crack width. By using soft cooling or hot charging process,the martensite transformation caused by rapid cooling could be prevented and granular bainite structure could be formed,which could control appearance and ex-tension of the internal crack.
参考文献
| [1] | 董瀚,曹文全,时捷,王存宇,王毛球,翁宇庆.第3代汽车钢的组织与性能调控技术[J].钢铁,2011(06):1-11. |
| [2] | SHI J;CAO W Q;DONG H.Ultra-fine grained high strength low alloy steel with high strength and high ductility[A].Switzerland:Trans Tech Publication,2010:238. |
| [3] | Sato M;Utsumi Y;Watanabe K .Ultra-high strength,quench type,hot rolled steel sheets of 1 620 MPa grade for automobile door impact beams[J].Kobelco Technology Review,2008,28(10):13. |
| [4] | Kwon O J;Lee K Y;Kim G S.New trends in advanced high strength steel development s for automotive application[A].Switzerland:Trans Tech Publica-tion,2010:136. |
| [5] | C.Y. Wang;J. Shi;W.Q. Cao;H. Dong .Characterization of microstructure obtained by quenching and partitioning process in low alloy martensitic steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(15):3442-3449. |
| [6] | 唐荻,米振莉,陈雨来.国外新型汽车用钢的技术要求及研究开发现状[J].钢铁,2005(06):1-5. |
| [7] | 米振莉,唐荻,严玲,郭锦.高强度高塑性TWIP钢的开发研究[J].钢铁,2005(01):58-60. |
| [8] | 纪云航,冯伟骏,王利,薛小怀.新一代高强度淬火分配钢的研究和应用[J].钢铁研究学报,2008(12):1-5. |
| [9] | 方园,梁高飞.高锰板带钢及其制造技术[J].钢铁,2009(01):1-6,66. |
| [10] | 张先棹.冶金传输原理[M].北京:冶金工业出版社,1991 |
| [11] | 徐祖耀.马氏体相变与马氏体[M].北京:科学出版社,1999 |
| [12] | 王力明 .Ni-Mn-Ga磁形状记忆合金定向凝固、马氏体相变及其应力分析[D].大连交通大学,2004. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%