连铸坯直接轧制生产特厚钢板时，由于压缩比的限制，很难生产出厚度超过100 mm的高质量钢板。采用复合轧制工艺可生产出厚度为260 mm的SM45复合钢板。对钢板进行探伤、冷弯、拉伸、冲击及硬度等试验检验其结合度和力学性能。结果表明，复合轧制生产的SM45钢板结合度良好，未发现明显的缺陷存在。钢板复合界面与基体的强度均在600 MPa以上；Z向试样的强度也达到600 MPa以上，断面收缩率在30%以上；冲击功在37 J以上。钢板不同位置处的基本组织都为铁素体与珠光体，但晶粒尺寸不同。复合界面处的组织为一条铁素体为主的带状组织，该组织的产生是由先共析铁素体导致的。
Heavy plates over 100 mm are hardly produced by continuous casting slab due to the restriction of reduction ra-tio.SM45 clad steel plate with thickness 260 mm was manufactured by clad rolling. Test methods,such as ultrasonic in-spection,cold bending,tensile,impact and hardness,were utilized to test the combination degree and mechanical proper-ties. The results showed that SM45 plate manufactured by clad rolling combined well and had no obvious defection. Strengths of clad interface and base body were both above 600 MPa. Z direction strengths were also above 600 MPa, and contraction of area were above 30%. Impact energy was above 37 J. The basic microstructure of SM45 steel plate was ferrite and pearlite,but the grain size was different in different locations. There was a ferrite belt in clad interface which formed because of the proeutectoid ferrite.
参考文献
| [1] | 王一德,唐荻,米振莉,吴华杰.中国特殊钢行业的发展现状及思考[J].钢铁,2013(07):1-6. |
| [2] | 于影霞,何柏林,李力.国内外模具材料的现状及发展趋势[J].热加工工艺,2009(02):45-48,97. |
| [3] | 耿明山,刘艳,黄衍林.大型特厚板坯料制造技术现状和发展趋势[J].中国冶金,2014(8):1-8. |
| [4] | 徐匡迪.中国特钢生产60年[J].钢铁,2014(07):2-7. |
| [5] | 许少普,崔冠军,吴彦,付全虎,杨东,赵迪.130mm特厚桥梁板Q345qD的开发[J].钢铁,2010(11):41-44. |
| [6] | 袁永旗,高照海,唐郑磊,李忠波,于飒,李亮亮.特厚合金结构钢板42CrMo的研制[J].钢铁,2012(04):102-105. |
| [7] | 李婧,赵德文,刘相华,何元春,隋鹤龙.高强度特厚板减量化轧制工艺[J].钢铁研究学报,2010(01):9-13. |
| [8] | 李忠波,许少普.高强度结构钢Q550D的研发实践[J].中国冶金,2013(09):19-21,58. |
| [9] | 杨东,唐郑磊,李红洋,张涛,徐昭.低合金结构钢Q345B 420mm特厚板的研发[J].中国冶金,2012(01):12-14,31. |
| [10] | NISHIDA Shun-ichi;MATSUOKA Toshio;WADA Tsunemi .Technology and Products of JFE Steel's Three Plate Mills[J].JFE technical report,2005(5):1-9. |
| [11] | 余伟,张烨铭,何春雨,徐立善,蔡庆伍.轧制复合生产特厚板工艺[J].北京科技大学学报,2011(11):1391-1395. |
| [12] | 骆宗安,谢广明,胡兆辉,贾涛,王国栋,王黎筠.特厚钢板复合轧制工艺的实验研究[J].塑性工程学报,2009(04):125-128. |
| [13] | WANG G L;LUO Z A;XIE G M et al.Experiment research on impact of total rolling reduction ratio on the properties of vacu-um rolling-bonding ultra-thick steel plate[J].Advanced Materi-als Research,2011,299:962. |
| [14] | 王储,胡昕明,高强,王文仲,梁福鸿.真空复合连铸板坯叠轧厚钢板工艺[J].金属热处理,2013(09):46-48. |
| [15] | 韦东滨,韩静涛,谢建新,付晨光,王连忠,贺毓辛.真空环境下钢中裂纹的高温愈合[J].金属学报,2000(07):713-717. |
| [16] | Masahiro N;Ikuro H;Shinji K et al.Effects of surface oxides of the phosphatability of the high strength cold rolled steels[J].Tet-su To Hagane,2006,92(06):378. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%