针对直弧型大型连铸机钢液中夹杂物更容易上浮到结晶器液面，有利于降低板坯中的夹杂物质量分数，生产宽厚板坯时角部容易出现横裂纹也容易出现纵裂纹的特点，重钢3号连铸机通过大倒角结晶器技术开发、直弧型连铸机对弧技术优化、板坯宽窄面鼓肚预防等工作降低坯壳所受到的应力；通过大倒角结晶器开发、二冷喷嘴布置优化、二冷动态配水等工作，使板坯温度避开钢的第三脆性区。这两方面综合作用的结果是，2014年2月至12月板坯角部裂纹率为零，解决了板坯角部横裂纹和纵裂纹问题。
For large-scale straight-curve type slab continuous caster,inclusions in moten steel are more likely to float to-wards the meniscus and be removed,which is help for the reduction of inclusions content in the strand. Meanwhile,the corner crack and longitudinal crack are easy to occur during the production of wide-thick slab. In the light of the above, Chongqing steel No.3 continuous caster developed some technologies,such as the adoption of chamfered mold,the im-provement of collating radian precision,the prevention of bulging on the narrow and wide faces,the optimization of the nozzles in secondary cooling zone and the dynamic secondary cooling water mode,to decrease the stress on the solidify-ing shell and make the strand away from the third brittle zone. From February to December 2014,the ratio of corner crack was zero,and the problems of corner crack and longitudinal crack have been solved.
参考文献
| [1] | 王明林;杨春政;陶红标;张慧;刘建华;吴夜明.微合金化钢连铸坯角部横裂纹形成机制[J].钢铁,2012(10):27-33,39. |
| [2] | 赵晶;甄新刚;朱志远;王玉龙;张虎成;赵新宇.倒角连铸坯角部纵向裂纹形成机制及控制[J].钢铁,2015(7):43-47. |
| [3] | 曹建新;陶红标;张慧;周明伟;张亮洲;彭明耀.倒角结晶器在涟钢板坯连铸生产中的应用[J].钢铁,2013(11):43-47. |
| [4] | 马范军;文光华;唐萍;韩靖.含铌、钒、钛微合金钢连铸坯角部横裂纹研究现状[J].材料导报,2010(5):89-91,95. |
| [5] | 王谦;鲁永剑;何宇明;胡兵;熊银成;张建国.提高宽厚板坯无清理率的关键技术[J].中国冶金,2012(12):22-27. |
| [6] | 王春怀;吴巍;干勇;何宇明;朱斌.含铌、钛船板钢高温塑性研究[J].钢铁,2002(8):49-52. |
| [7] | 刘洋;王文军;朱志远;王凤琴;关春阳;韦耀环.利用倒角结晶器消除连铸板坯的角横裂纹缺陷[J].钢铁,2012(4):47-50. |
| [8] | 何宇明,胡兵,张慧,周宏,王玫,潘时松,陶红标.大倒角结晶器在宽厚板坯连铸机上的应用[C].第九届中国钢铁年会论文集,2013:1-7. |
| [9] | 任飞飞;张慧;王伟宁;王明林.倒角结晶器铜板实际温度场数值仿真[J].钢铁,2015(4):27-33. |
| [10] | 赵艳玲;王淑满;王洪兴;常立山.X80管线钢的生产实践[J].中国冶金,2014(8):17-21. |
| [11] | 赵磊;何宇明;潘时松;田陆;彭高;邢保龙.目标温度动态控制二冷配水的研究[J].连铸,2012(6):8-12. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%