利用C型缺口试样研究了不同淬透性的SAE8620H齿轮钢的渗碳热处理变形,并对C型缺口试样心部微观组织和硬度进行了分析.结果表明,SAE8620H齿轮钢在距淬火端9 mm处的硬度低于32HRC时,C型缺口试样心部主要为贝氏体组织,渗碳热处理变形较小;随着淬透性的提高,试样心部马氏体组织逐渐增加,渗碳热处理变形显著增大.不同淬透性的SAE8620H齿轮钢的相变组织不同,因而渗碳热处理变形不同.

Effect of hardenability on distortion by heat treatment for SAE8620H gear steel was investigated by means of Navy-C ring specimens after carburization.Meanwhile,the microstructures and hardness in the centers of cross sections of C-ring specimens were analysed.The results show that when the hardness value at the distance of 9 mm from quenched end in Jominy test is below 32HRC,there is mainly bainite in the center of cross section of C-ring specimen,which has small distortion by heat treatment.The volume fraction of martensite in the center of cross section of C-ring specimen increases when the hardness value at the distance of 9 mm from quenched end increases from 32HRC to 35HRC.The distortion by heat treatment of SAE8620H steel increases slowly in the original stage and rapidly in the subsequent stage with increase of the hardness value at the distance of 9 mm from quenched end due to difference in phase transformation.

参考文献

[1] 安金敏;覃明;丁毅.奥氏体晶粒度对汽车齿轮钢热处理畸变的影响[J].热处理,2013(3):48-51.
[2] 陈国民.对齿轮热处理畸变控制技术的评述[J].金属热处理,2012(02):1-13.
[3] 张熹;崔京玉;章军.浅析齿轮钢及热处理工艺对汽车用齿轮性能的影响[J].钢铁研究学报,2009(10):38-42.
[4] 陈晖;周细应.汽车齿轮钢的研究进展[J].材料科学与工程学报,2011(3):478-482.
[5] 吴奇;潘晓东.高淬透性材料齿轮热处理变形的控制[J].机械传动,2014(10):78-80,107.
[6] A.D. da Silva;T.A. Pedrosa;J.L. Gonzalez-Mendez;X. Jiang;P.R. Cetlin;T. Altan.Distortion in quenching an AISI 4140 C-ring - Predictions and experiments[J].Materials & design,2012Dec.(Dec.):55-61.
[7] C.M. Amey;H. Huang;P.E.J. Rivera-Diaz-del-Castillo.Distortion in 100Cr6 and nanostructured bainite[J].Materials & design,2012Mar.(Mar.):66-71.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%