某线材厂SWRM6的热轧盘条在用户使用拉拔后发生了断裂。通过取样对该盘条进行了断口宏观形貌、金相微观组织、缺陷及电子探针能谱方面的分析，表明断裂盘条的试样边部均存在裂纹，裂纹处有夹渣，夹渣碳质量分数远远高于基体碳质量分数。由于夹渣的存在，一方面因为其塑性较钢材低，在轧制和拉拔时易形成开裂，另一方面由于其富碳层使基体表面增碳，形成索氏体和网状碳化物等异常组织，加速了盘条拉拔时的断裂。
Fracture of the SWRM6 wire coil occurred after the customer drawing .The investigations of the test of macroscopic observation ,metallographic microstructure analysis and EMPA analysis showed that there were cracks existed at the margin of the sample and there were slags where the carbon content was higher than the basal body lied at the side of the cracks .Because of the existence of slags ,on one hand the low plasticity led to the cracking during rolling and drawing ,on the other hand ,the formation of abnormal tissue martensite and carbide network due to the carburizing from rich carbon layer to the substrate surface accelerated the fracture during drawing .
参考文献
| [1] | 杨浩,唐萍,孙维,汪开忠,吴坚,许建,张杰新.优化保护渣改善冷镦钢铸坯表面质量[J].钢铁钒钛,2010(02):88-92. |
| [2] | 胡海红,李静,王福明,张作泰.CaO-SiO_2-Al_2O_3-Na_2O-CaF_2固态渣系的再结晶性能[J].钢铁研究学报,2012(07):13-18. |
| [3] | 林晏民,欧阳民,廖美华,姚铁梅.保护渣高温特性对板坯表面裂纹影响的研究[J].中国冶金,2011(08):26-29. |
| [4] | HE Sheng-ping,HUANG Qing-yun,ZHANG Guo-xing,LU Yong-jian,WANG Qian.Solidification Properties of CaO-SiO2-TiO2 Based Mold Fluxes[J].钢铁研究学报：英文版,2011(07):15-19,52. |
| [5] | 姜茂发,刘承军,王云盛,朱英雄.超低碳钢连铸保护渣的发展[J].炼钢,2000(03):52-55,60. |
| [6] | 吴杰;李正邦;林功文 .结晶器保护渣对超低碳钢增碳的影响[J].钢铁研究学报,1999,11(1):66. |
| [7] | 铁生年,张芬娟,陈列,李昀珺,李星.连铸保护渣性能研究进展[J].中国冶金,2008(12):1-5. |
| [8] | 杜恒科,文光华,唐萍,姚永宽,耿建林,王桂玲,张悦.宽板坯结晶器中碳钢保护渣研究[J].中国冶金,2006(07):37-40. |
| [9] | 周鉴,王强,仇圣桃,干勇.高铝钢连铸保护渣结晶矿相的研究[J].钢铁研究学报,2013(04):15-19,24. |
| [10] | 廖鹏,王强,仇圣桃,张兴中.保护渣膜传热测量装置的开发与研究[J].钢铁研究学报,2013(01):59-62. |
| [11] | 张彦文,王继辉,张友登.SWRM6盘条断裂原因分析[J].武汉工程职业技术学院学报,2009(03):27-28. |
| [12] | 桂仙;陈士华;浦绍康.钢铁产品缺陷与失效实例分析图谱[M].北京:冶金工业出版社,2012 |
| [13] | 申丽娟,万长杰,李国军,薛佳鹏.预应力钢绞线SWRH82B断裂分析[J].河南冶金,2012(06):22-24. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%