针对浮动催化化学气相沉积(CVD)法制备的碳纳米管(CNTs)膜,首先采用红外光谱表征分析了包覆在CNTs表面的无定形物质的组成,然后分别采用热处理和酸洗处理方法,考察了CNTs膜中无定形物和残留Fe催化剂对CNTs膜拉伸取向行为的影响.结果表明:采用CVD法制备的CNTs膜中CNTs表面无定形物为含氧或烷烃、烯烃类低聚物,可通过350℃有氧热处理基本去除.该CNTs膜的牵伸取向重排行为受组成影响显著,CNTs表面的低聚物可增强CNTs的管间黏结作用,Fe催化剂颗粒成为CNTs网络结构的交联结点,两者均有利于提高CNTs的取向程度和聚并成束的尺寸,进而提高CNTs膜的拉伸稳定性和断裂韧性.牵伸取向后CNTs膜与环氧树脂溶液的浸润性提高,其CNTs膜/环氧复合材料的拉伸强度和模量达到1 228 MPa和94.5 GPa,相比初始无规CNTs膜/环氧复合材料的分别提高了337％和729％.
参考文献
| [1] | Eric Pop;David Mann;Qian Wang;Kenneth Goodson;Hongjie Dai.Thermal Conductance of an Individual Single-Wall Carbon Nanotube above Room Temperature[J].Nano letters,20061(1):96-100. |
| [2] | Peng B;Locascio M;Zapol P;Li SY;Mielke SL;Schatz GC;Espinosa HD.Measurements of near-ultimate strength for multiwalled carbon nanotubes and irradiation-induced crosslinking improvements[J].Nature nanotechnology,200810(10):626-631. |
| [3] | Ozaki T.;Mitani T.;Iwasa Y..Stiffness of single-walled carbon nanotubes under large strain[J].Physical review letters,20008(8):1712-1715. |
| [4] | Li Song;Lijie Ci;Li Lv;Zhenping Zhou;Xiaoqin Yan;Dongfang Liu;Huajun Yuan;Yan Gao;Jianxiong Wang;Lifeng Liu;Xiaowei Zhao;Zengxing Zhang;Xinyuan Dou;Weiya Zhou;Gang Wang;Chaoyin Wang;Sishen Xie.Direct Synthesis of a Macroscale Single-Walled Carbon Nanotube Non-Woven Material[J].Advanced Materials,200417(17):1529-1534. |
| [5] | Ma WJ;Song L;Yang R;Zhang TH;Zhao YC;Sun LF;Ren Y;Liu DF;Liu LF;Shen J.Directly synthesized strong, highly conducting, transparent single-walled carbon nanotube films[J].Nano letters,20078(8):2307-2311. |
| [6] | 刘妍;李敏;刘千立;顾轶卓;李艳霞;张佐光.多壁巴基纸／环氧复合材料拉伸性能的影响因素[J].复合材料学报,2012(6):26-31. |
| [7] | Li YL;Kinloch IA;Windle AH.Direct spinning of carbon nanotube fibers from chemical vapor deposition synthesis[J].Science,20045668(5668):276-278. |
| [8] | Xiao-Hua Zhong;Ya-Li Li;Ya-Kun Liu;Xiao-Hua Qiao;Yan Feng;Ji Liang;Jun Jin;Lu Zhu;Feng Hou;Jin-You Li.Continuous MuItilayered Carbon Nanotube Yarns[J].Advanced Materials,20106(6):692-696. |
| [9] | Wang D;Song PC;Liu CH;Wu W;Fan SS.Highly oriented carbon nanotube papers made of aligned carbon nanotubes[J].Nanotechnology,20087(7):75609-1-75609-6-0. |
| [10] | Di, J.;Hu, D.;Chen, H.;Yong, Z.;Chen, M.;Feng, Z.;Zhu, Y.;Li, Q..Ultrastrong, foldable, and highly conductive carbon nanotube film[J].ACS nano,20126(6):5457-5464. |
| [11] | Xin Wang;Philip D. Bradford;Wei Liu;Haibo Zhao;Yoku Inoue;Jon-Paul Maria;Qingwen Li;Fuh-Gwo Yuan;Yuntian Zhu.Mechanical and electrical property improvement in CNT/Nylon composites through drawing and stretching[J].Composites science and technology,201114(14):1677-1683. |
| [12] | Qianli Liu;Min Li;Yizhuo Gu.Highly aligned dense carbon nanotube sheets induced by multiple stretching and pressing[J].Nanoscale,20148(8):4338-4344. |
| [13] | High Mechanical Performance Composite Conductor: Multi-Walled Carbon Nanotube Sheet/Bismaleimide Nanocomposites[J].Advanced functional materials,200920(20):3219. |
| [14] | Ya-Nan Liu;Min Li;Yizhuo Gu.A modified spray-winding approach to enhance the tensile performance of array-based carbon nanotube composite films[J].Carbon: An International Journal Sponsored by the American Carbon Society,2013:187-195. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%