为探索超声辅助下利用紫外光及耦合热还原工艺制备RGO/纳米TiO2复合材料的方法,并对其在缺氧水体中的光催化还原特性进行研究,首先,以鳞片石墨为原料,采用改进的Hummers法制备了氧化石墨烯(GO),进而通过超声/紫外光还原工艺制备了还原氧化石墨烯(RGO);然后,以钛酸丁脂和RGO为前驱物,采用溶胶-凝胶法并在氮气保护下高温加热制备了RGO/纳米TiO2复合光催化材料;接着,利用FTIR、XRD、BET及紫外-可见光谱等对RGO/纳米TiO2复合材料进行了结构性能表征;最后,以2,4-二氯苯氧乙酸(2,4-D)为探针物,研究了RGO/纳米TiO2在缺氧水体中的光催化特性与2,4D降解机制.结果表明:采用低温氧化Hummers法制备的GO六碳环上生成的活性基团较少,采用超声/紫外光还原工艺及耦合高温热还原工艺可使环状结构得到良好的修复;所制备的RGO/纳米TiO2复合材料具有良好的2,4D降解能力,在缺氧状态下,2,4-D主要发生光催化还原反应,脱除苯环上的氯,产生氯酚、邻苯三酚及间苯三酚等中间产物,部分2,4-D被氧化降解生成CO2和H2O.制备的RGO/纳米TiO2复合材料具有良好的光催化还原性能.
参考文献
[1] | 任芳;朱光明;任鹏刚.纳米石墨烯复合材料的制备及应用研究进展[J].复合材料学报,2014(2):263-272. |
[2] | Sasha Stankovich;Dmitriy A. Dikin;Richard D. Piner.Synthesis of graphene-based nanosheets via chemical reduction of exfoliated graphite oxide[J].Carbon: An International Journal Sponsored by the American Carbon Society,20077(7):1558-1565. |
[3] | O. Akhavan;E. Ghaderi.Photocatalytic Reduction of Graphene Oxide Nanosheets on TiO2 Thin Film for Photoinactivation of Bacteria in Solar Light Irradiation[J].The journal of physical chemistry, C. Nanomaterials and interfaces,200947(47):20214-20220. |
[4] | Li D;Muller MB;Gilje S;Kaner RB;Wallace GG.Processable aqueous dispersions of graphene nanosheets[J].Nature nanotechnology,20082(2):101-105. |
[5] | Nicholas A. Kotov;Imre Dekany;Janos H. Fendler.Ultrathin Graphite Oxide-Polyelectrolyte Composites Prepared by Self-Assembly: Transition Between Conductive and Non-Conductive States[J].Advanced Materials,19968(8):637-641. |
[6] | Sung Mook Choi;Min Ho Seo;Hyung Ju Kim.Synthesis of surface-functionalized graphene nanosheets with high Pt-loadings and their applications to methanol electrooxidation[J].Carbon: An International Journal Sponsored by the American Carbon Society,20113(3):904-909. |
[7] | Zhai Qianqian;Bo Tang;Hu Guoxin.High photoactive and visible-light responsive graphene/titanate nanotubes photocatalysts: Preparation and characterization[J].Journal of hazardous materials,2011:78-86. |
[8] | 王思雨;潭欣;于涛.TiO2-石墨烯(Gn)复合材料光催化降解O3研究[J].环境科学学报,2014(2):325-330. |
[9] | 周琪;钟永辉;陈星;王岩;刘平;吴玉程.石墨烯/纳米TiO2复合材料的制备及其光催化性能[J].复合材料学报,2014(2):255-262. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%