使用2种硅烷偶联剂(KH550和KH792)对介孔分子筛MCM-41进行表面改性,采取氮气吸附-脱附、FTIR和TGA等进行表征,并采用原位聚合法制备了MCM-41/环氧树脂复合材料,研究了偶联剂种类和MCM-41用量等对复合材料固化过程及性能的影响.结果表明:硅烷偶联剂可与MCM-41表面的硅羟基反应,在分子筛内外表面接枝上功能化基团.经表面修饰的MCM-41比表面积下降为原来的1/5,KH550在MCM-41表面接枝率仅为KH792的一半.KH550与MCM-41外表面反应得更充分,KH792对MCM-41孔道内壁的修饰效果更强.固化动力学结果表明:KH792的功能化基团有伯胺和仲胺,与环氧树脂具有更高的反应活性,但不利于环氧大分子进入孔道,仅以球形粒子的形式添加在环氧树脂中;KH550表面修饰的MCM-41可使环氧大分子进入孔道内形成互穿结构.KH550表面修饰体系更多体现出MCM-41多孔的特征,形成了有机-无机互穿结构的复合体系,大幅度提高了储能模量和玻璃化转变温度.KH792表面修饰体系则呈常规球形纳米粒子的特征,其储能模量和玻璃化转变温度较纯环氧树脂有所提高但幅度不大.
参考文献
[1] | 张莉莉;黄思共;李湘祁.介孔MCM-48粉体对环氧树脂性能影响[J].热固性树脂,2009(6):41-43,49. |
[2] | 王娜;张静;戴彩云;富露祥.环氧树脂/纳米介孔分子筛复合材料的制备及性能研究[J].工程塑料应用,2006(5):15-18. |
[3] | 王娜;李明天;张军旗;张劲松.MCM-41填加量与偶联修饰对复合材料拉伸性能的影响[J].复合材料学报,2005(2):27-33. |
[4] | 曹均助;苏跃增;周持兴.介孔材料SBA-15/环氧树脂复合材料的制备和固化动力学[J].高分子材料科学与工程,2011(11):133-136. |
[5] | Lin JJ;Wang XD.Preparation, microstructure, and properties of novel low-kappa brominated epoxy/mesoporous silica composites[J].European Polymer Journal,20085(5):1414-1427. |
[6] | BRIAN G.TREWYN;IGOR I.SLOWING;SUPRATIM GIRI.Synthesis and Functionalization of a Mesoporous Silica Nanoparticle Based on the Sol-Gel Process and Applications in Controlled Release[J].Accounts of Chemical Research,20079(9):846-853. |
[7] | Save M;Granvorka G;Bernard J;Charleux B;Boissiere C;Grosso D;Sanchez C.Atom transfer radical polymerization of styrene and methyl methacrylate from mesoporous ordered silica particles[J].Macromolecular rapid communications: Publishing the newsletters of the European Polymer Federation,20066(6):393-398. |
[8] | Liu WB;Qiu QH;Wang J;Huo ZC;Sun H.Curing kinetics and properties of epoxy resin-fluorenyl diamine systems[J].Polymer: The International Journal for the Science and Technology of Polymers,200820(20):4399-4405. |
[9] | Yuanxin Zhou;Farhana Pervin;Lance Lewis.Experimental study on the thermal and mechanical properties of multi-walled carbon nanotube-reinforced epoxy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20070(0):657-664. |
[10] | Shi, HW;Liu, FC;Yang, LH;Han, EH.Characterization of protective performance of epoxy reinforced with nanometer-sized TiO2 and SiO2[J].Progress in Organic Coatings,20084(4):359-368. |
[11] | Lin CH;Feng CC;Hwang TY.Preparation, thermal properties, morphology, and microstructure of phosphorus-containing epoxy/SiO2 and polyimide/SiO2 nanocomposites[J].European Polymer Journal,20073(3):725-742. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%