由于复合材料具有组成多元、各向异性等特点,电热载荷作用下碳纤维复合材料内部的响应行为十分复杂.为了研究碳纤维复合材料的电热响应,首先采用自制电热损伤试验平台,测试了不同电流强度下碳纤维复丝试样的表面温度分布,获得了碳纤维复丝电阻随温度的变化规律,初步揭示了碳纤维复丝具有温敏效应.然后,考察了不同电流处理条件下碳纤维复丝拉伸强度、断裂伸长率和拉伸模量的变化规律,并运用SEM和FTIR对电流处理前后材料的形貌和微观结构变化进行了分析.研究结果表明:纤维在通电过程中的产热效应促进了基体的进一步固化,同时提高了复丝界面的粘结性能;然而,当电流强度过大时,复丝的拉伸强度会因纤维本体的损伤或基体及界面层的烧蚀破坏而降低,从而降低了碳纤维复合材料的性能.
参考文献
| [1] | An integrated method for predicting damage and residual tensile strength of composite laminates under low velocity impact[J].Computers & structures,20097/8(7/8):456-466. |
| [2] | Yoshiyasu Hirano;Shingo Katsumata;Yutaka Iwahori;Akira Todoroki.Artificial lightning testing on graphite/epoxy composite laminate[J].Composites, Part A. Applied science and manufacturing,201010(10):1461-1470. |
| [3] | A. Barakati;O. I. Zhupanska.Influence of the electric current waveform on the dynamic response of the electrified composites[J].International journal of mechanics and materials in design,20131(1):11-20. |
| [4] | RE. Deierling;O.I. Zhupanska.Experimental study of high electric current effects in carbon/epoxy composites[J].Composites science and technology,201114(14):1659-1664. |
| [5] | MARCO GIGLIOTTI;MARIE-CHRISTINE LAFARIE-FRENOT;JEAN-CLAUDE GRANDIDIER.Development of experimental and modelling tools for the characterisation of the thermo-electro-mechanical behaviour of composite materials for aircraft applications[J].Mecanique & industries,20112(2):87-101. |
| [6] | Toshio Ogasawara;Yoshiyasu Hirano;Akinori Yoshimura.Coupled thermal-electrical analysis for carbon fiber/epoxy composites exposed to simulated lightning current[J].Composites, Part A. Applied science and manufacturing,20108(8):973-981. |
| [7] | von Klemperer, Christopher J.;Maharaj, Denver.Composite electromagnetic interference shielding materials for aerospace applications[J].Composite structures,20094(4):467-472. |
| [8] | 黄莉;龚学进;孙明清;陈龙.连续碳纤维带树脂基复合材料的传感性能实验研究[J].功能材料,2010(8):1402-1405. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%