以1,3-二(4-羟基苯基)金刚烷(BHPA)和环氧氯丙烷(ECH)为原料,采用二步法合成了低分子量的1,3-二(4-羟基苯基)金刚烷二缩水甘油醚(DGEBAD),采用 FTIR、1 H-NMR和凝胶渗透色谱(GPC)分别对其结构和分子量进行了表征并滴定得到其环氧值；采用旋转流变仪对其流变性能进行了表征。使用4,4’-二氨基二苯基甲烷(DDM)固化DGEBAD,对固化DGEBAD-DDM树脂体系的力学性能、吸水率和耐热性进行了测试,得到的固化物的拉伸强度为90 MPa,玻璃化转变温度为163℃,5%热失重温度高达401℃,吸水率比相同条件下环氧树脂 E51-DDM固化物降低了31.60%。
The diglycidyl ether of 1,3-bis (4-hydroxyphenyl)adamantane(DGEBAD)with low molecular weight was synthesized from 1,3-bis (4-hydroxyphenyl)adamantane (BHPA)and epichlorohydrin (ECH)by two-step method.The structure and molecular weight were confirmed by FTIR,1 H-NMR and gel permeation chromatogra-phy(GPC),and epoxy value was obtained by titration.The rheology property was also characterized by rotational rheometer.DGEBAD was cured with 4,4’-diaminodiphenyl methane (DDM).The mechanical properties,water ab-sorption rate and heat resistance characteristics of the cured DGEBAD-DDM resin system were investigated.The tensile strength and the glass transition temperature of the cured DGEBAD-DDM resin system is 90 MPa and 163 ℃,respectively and 5% mass loss temperature occurs at up to 401 ℃.The water absorption rate of the cured DGEBAD-DDM decreases by 31.60% compared to the cured epoxy resin E51-DDM.
参考文献
| [1] | 王永杰.金刚烷--新一代化工原料[J].价值工程,2010(25):128-129. |
| [2] | 刘卅;郭建维.含金刚烷聚合物的研究进展[J].高分子材料科学与工程,2008(7):6-10. |
| [3] | Chern YT.;Kao SC.;Shiue HC..Synthesis and characterization of new polyamides containing adamantyl and diamantyl moieties in the main chain[J].Journal of Polymer Science, Part A. Polymer Chemistry,19985(5):785-792. |
| [4] | Hsiao SH.;Li CT..Synthesis and characterization of new adamantane-based polyimides[J].Macromolecules,199821(21):7213-7217. |
| [5] | Pixton MR.;Paul DR..GAS TRANSPORT PROPERTIES OF ADAMANTANE-BASED POLYSULFONES[J].Polymer: The International Journal for the Science and Technology of Polymers,199516(16):3165-3172. |
| [6] | 潘莉辉;郭建维;王岳琴;钟星;崔英德.金刚烷基磺酸盐阻燃剂的制备及在聚碳酸酯中的应用[J].高分子材料科学与工程,2014(6):101-105. |
| [7] | 熊明;高斯;杨小平;吕亚非;李鹏.含金刚烷结构胺类固化剂的制备与性能[J].高分子材料科学与工程,2014(10):133-138. |
| [8] | 孟运东;苏小明;井新利.含金刚烷结构新型环氧树脂的合成[J].热固性树脂,2010(1):26-29. |
| [9] | Su XM;Jing XL.Novel adamantane-containing epoxy resin[J].Journal of Applied Polymer Science,20072(2):737-742. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%