通过施加动态边界条件和超声振动热效应转化相结合的方法近似处理超声振动边界条件,研究了超声作用下激光熔覆 SiC/316 L复合涂层的残余应力,并探讨了超声振幅和扫描速度对复合涂层残余应力的影响。根据优化结果采用超声辅助激光熔覆制备 SiC/316 L复合涂层。结果表明：超声振幅和扫描速度对涂层表面x方向应力、y方向应力、界面处剪切应力和 von Mises 应力均有明显影响。当超声振幅为10μm,扫描速度为10 mm/s时,SiC/316L复合涂层有较好的残余应力缓和效果。超声空化或机械效应及声流作用促使 SiC/316L复合涂层组织得到明显细化,且 SiC颗粒均匀分布。
By combining ultrasonic vibration thermal effects conversion with dynamic boundary conditions imposed, the ultrasonic vibration boundary conditions were made approximation.The residual stress of SiC/316L composite coating with ultrasonic vibration in laser cladding was investigated,and the influence of ultrasonic amplitude and scanning speed on residual stress of composite coating was studied.According to the optimization results,SiC/316L composite coating was prepared by ultrasonic aided laser cladding.The results show that ultrasonic amplitude and scanning speed have significant effects on x-stress,y-stress,shear stress at the interface and von Mises stress on the coating surface.The residual stress relaxation of SiC/316L composite coating is excellent when the ultrasonic ampli-tude is 10μm and scanning speed is 10 mm/s.The structure of coating is obvious refinement,and SiC particles is uniform distributed for the ultrasonic cavitation or mechanical effect and acoustic streaming effect.
参考文献
| [1] | 樊新民;任小敏.316L不锈钢表面耐高温氧化涂层的制备与性能[J].材料科学与工艺,2014(1):105-109. |
| [2] | Zhang K;Liu WJ;Shang XF.Research on the processing experiments of laser metal deposition shaping[J].Optics & Laser Technology,20073(3):549-557. |
| [3] | 李德英;张坚;赵龙志;赵明娟.激光熔覆Fe-Al-Si复合涂层研究[J].热加工工艺,2012(24):162-164,167. |
| [4] | 吴东江;吴楠;杨策;马广义;康仁科.预热对Al2O3陶瓷激光熔覆层温度梯度影响的模拟[J].稀有金属材料与工程,2013(10):2039-2042. |
| [5] | Masaki Sumida;Sanghoon Jung;Toshimitsu Okane.Microstructure, solute partitioning and material properties of gadolinium-doped magnesium alloy AZ91D[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20091/2(1/2):903-910. |
| [6] | 陈宏;李铸国;姚成武;吴毅雄.Gd元素对激光熔覆镁合金涂层组织和性能的影响[J].中国激光,2015(3):198-204. |
| [7] | 翁子清;董刚;张群莉;郭士锐;姚建华.退火对激光熔覆FeCrNiCoMn高熵合金涂层组织与性能的影响[J].中国激光,2014(3):59-64. |
| [8] | V. Cannillo;M. Montorsi;C. Siligardi.Microscale computational simulation and experimental measurement of thermal residual stresses in glass-alumina functionally graded materials[J].Journal of the European Ceramic Society,20068(8):1411-1419. |
| [9] | Xinbao Liu;Yoshiaki Osawa;Susumu Takamori;Toshiji Mukai.Grain refinement of AZ91 alloy by introducing ultrasonic vibration during solidification[J].Materials Letters,200817/18(17/18):2872-2875. |
| [10] | 乐启炽;张志强;崔建忠;刘鸿明;高恩保.超声孕育处理对AS41镁合金凝固组织的影响[J].中国有色金属学报,2010(5):813-819. |
| [11] | 陈畅源;邓琦林;宋建丽.超声振动对激光熔覆过程的影响[J].电加工与模具,2005(3):37-40. |
| [12] | 李德英;赵龙志;张坚;姜羡.超声振动对激光熔覆 TiC／FeAl复合涂层温度场的影响[J].金属热处理,2015(3):190-194. |
| [13] | 钦兰云;王维;杨光.超声辅助钛合金激光沉积成形试验研究[J].中国激光,2013(1):76-81. |
| [14] | 龚伟;周黎明;王恩泽.Y-TZP/LZAS微晶玻璃功能梯度涂层残余应力的有限元分析[J].材料研究学报,2014(10):787-793. |
| [15] | 邓志成 .超声辅助激光熔注复合涂层晶粒生长研究[D].华东交通大学,2015. |
| [16] | 贺儒;闫洪.超声处理对原位Mg2Si/AM60复合材料的影响[J].特种铸造及有色合金,2012(7):657-660. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%