通过理论计算,探究Cf/SiC复合材料密度与C/C坯体密度的相关性;而后采用碳纤维布叠层制作2DC/C坯体,经先驱体浸渍裂解工艺增密,制得密度分别为0.98、1.06、1.12 g/cm3的C/C坯体,通过液相渗硅法反应合成2D CJSiC复合材料,探究C/C坯体密度对其结构和性能的影响.与理论计算结果来对比.研究结果表明:试验结果与理论数学计算结果基本一致.随着C/C坯体密度的增加,Cf/SiC复合材料的密度出现先上升后下降的趋势,当C/C坯体密度大于0.98 g/cm3后,复合材料的弯曲强度随着C/C坯体密度的增加而降低,C/C坯体密度为0.98 g/cm3时,2D CJSiC复合材料结构和性能较优.
参考文献
| [1] | 张红波;尹健;熊翔.C/C复合材料烧蚀性能的研究进展[J].材料导报,2005(7):97-99,103. |
| [2] | 黄海明;杜善义;吴林志;王建新.C/C复合材料烧蚀性能分析[J].复合材料学报,2001(3):76-80. |
| [3] | 迟伟东;沈曾民;张学军;刘辉;于建民.由炭布制备C/C复合材料工艺及性能的研究[J].新型炭材料,2001(4):55-57. |
| [4] | 王静;曹英斌;刘荣军;张德坷;严春雷.C/C-SiC复合材料的反应烧结法制备及应用进展[J].材料导报,2013(5):29-33. |
| [5] | MANISH PATEL;KUMAR SAURABH;V V BHANU PRASAD.High temperature C/C-SiC composite by liquid silicon infiltration: a literature review[J].Bulletin of Materials Science,20121(1):63-73. |
| [6] | Krenkel W;Berndt F.C/C-SiC composites for space applications and advanced friction systems[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20051/2(1/2):177-181. |
| [7] | 谢建伟 .C/SiC复合材料的结构与力学性能[D].中南大学,2007. |
| [8] | 马青松;刘海韬;潘余;刘卫东;陈朝辉.C/SiC复合材料在超燃冲压发动机中的应用研究进展[J].无机材料学报,2013(03):247-255. |
| [9] | Qing Zhou;Shaoming Dong;Yusheng Ding.Three-dimensional carbon fiber-reinforced silicon carbide matrix composites by vapor silicon infiltration[J].CERAMICS INTERNATIONAL,20096(6):2161-2169. |
| [10] | 何柏林;孙佳.碳纤维增强碳化硅陶瓷基复合材料的研究进展及应用[J].硅酸盐通报,2009(6):1197-1202,1207. |
| [11] | 闫联生;崔红;李克智;李贺军;王涛;宋麦丽.炭纤维针刺预制体增强C/SiC复合材料的制备与性能研究[J].无机材料学报,2008(2):223-228. |
| [12] | Honglei, W.;Xingui, Z.;Jinshan, Y.;Yingbin, C.;Rongjun, L..Microstructure, mechanical properties and reaction mechanism of KD-1 SiC_f/SiC composites fabricated by chemical vapor infiltration and vapor silicon infiltration[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20116(6):2441-2445. |
| [13] | Li, G.;Zhang, C.;Hu, H.;Zhang, Y..Preparation and mechanical properties of C/SiC nuts and bolts[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2012:1-5. |
| [14] | 彭可;葛毅成;杨琳;易茂中.C/C坯体密度对熔融渗硅法制备的C/C-SiC复合材料摩擦行为的影响[J].粉末冶金材料科学与工程,2010(3):252-257. |
| [15] | 王继平;金志浩;钱军民;乔冠军.反应熔渗法制备C/C-SiC复合材料及其反应机理和动力学的研究进展[J].硅酸盐学报,2005(9):1120-1126. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%