采用静电纺丝技术制备聚乙烯醇/二氧化钛复合纳米纤维膜,利用戊二醛对复合纳米纤维膜进行改性.分析改性前后材料表面形貌、表面化学基团的变化及其耐水性和热性能.结果表明:复合纳米纤维表面粗糙度随二氧化钛含量的增大而增大.改性后纤维形貌保持不变,纤维间出现粘结,材料表面发生羟醛缩合反应,在1600cm-1处出现-C=C红外特征峰,复合纳米纤维膜耐水性显著提高,材料在190℃处的熔融峰消失.
参考文献
[1] | 马贵平;方大为;刘洋;陈洁;聂俊.电纺丝制备纳米纤维及其应用[J].材料科学与工程学报,2012(2):312-323. |
[2] | Zheng-Ming Huang;Y.-Z. Zhang;M. Kotaki.A review on polymer nanofibers by electrospinning and their applications in nanocomposites[J].Composites science and technology,200315(15):2223-2253. |
[3] | 丁源维;王騊;姚菊明;王晟.静电纺制备TiO2/PVA复合纳米纤维及其光催化性能研究[J].浙江理工大学学报,2013(1):31-35. |
[4] | Costa, R.G.F.;Ribeiro, C.;Mattoso, L.H.C..Study of the effect of rutile/anatase TiO_2 nanoparticles synthesized by hydrothermal route in electrospun PVA/TiO_2 nanocomposites[J].Journal of Applied Polymer Science,20136(6):4463-4469. |
[5] | Saeed Abbasizadeh;Ali Reza Keshtkar;Mohammad Ali Mousavian.Preparation of a novel electrospun polyvinyl alcohol/titanium oxide nanofiber adsorbent modified with mercapto groups for uranium(VI) and thorium(IV) removal from aqueous solution[J].Chemical engineering journal,2013:161-171. |
[6] | Lee, K.;Lee, S..Multifunctionality of poly(vinyl alcohol) nanofiber webs containing titanium dioxide[J].Journal of Applied Polymer Science,20125(5):4038-4046. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%