采用双主相合金技术制备了含Ce烧结钕铁硼磁体.Ce元素替代传统Nd/Dy元素总量的15%时,含Ce磁体具有良好的失重率,明显优于商业用N33和N45磁体.通过测量磁体在NaOH溶液中的极化曲线表明,含Ce磁体的腐蚀电位和腐蚀电流密度均好于商业用N33和N45磁体.SEM分析显示,含Ce磁体的晶粒尺寸明显小于其他商业用磁体,并且富钕相更加细小,分布均匀.含Ce磁体具有良好耐蚀性的主要原因是:Ce的加入,细化的晶粒,减小了富钕相尺寸,进而提高了磁体的腐蚀电位.
参考文献
[1] | Pei WL.;He CS.;Lian FZ.;Zhou GQ.;Yang HC. .Structures and magnetic properties of sintered Nd-Fe-B magnets produced by strip casting technique[J].Journal of Magnetism and Magnetic Materials,2002(1/3):475-478. |
[2] | W.F. Li;H. Sepehri-Amin;T. Ohkubo .Distribution of Dy in high-coercivity (Nd,Dy)-Fe-B sintered magnet[J].Acta materialia,2011(8):3061-3069. |
[3] | 朱明刚,方以坤,李卫.高性能Nd-Fe-B复合永磁材料微磁结构与矫顽力机制[J].中国材料进展,2013(02):65-73,101. |
[4] | 刘卫强,岳明,张久兴,王公平,李涛.富钕相对烧结NdFeB磁体耐腐蚀性的影响[J].稀有金属材料与工程,2007(06):1066-1069. |
[5] | M. Yue;J. X. Zhang;W. Q. Liu .Chemical stability and microstructure of Nd-Fe-B magnet prepared by spark plasma sintering[J].Journal of Magnetism and Magnetic Materials,2004(2/3):364-368. |
[6] | 张雪峰,史孟飞,李培忠,戴永峰,马强,李永峰.Ce对NdFeB永磁体磁性能和微观结构的影响[J].稀土,2013(04):12-16. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%