目的：研究不同机械研磨处理条件对AZ91 D镁合金表面晶粒细化行为与机制的影响。方法采用不同直径的弹丸对密排六方结构的AZ91 D镁合金进行不同时间的表面机械研磨处理,对处理试样的表面显微结构进行对比和表征,分析晶粒细化机制。结果通过表面机械研磨处理可以实现AZ91 D镁合金的表层晶粒细化。在一定范围内,弹丸直径越大,处理时间越长,表层晶粒细化就越明显,晶粒尺寸可细化至约24nm。结论 AZ91D镁合金表面机械研磨处理晶粒细化是孪生和位错滑移的综合结果。选择弹丸直径16 mm,处理时间180 min的工艺参数,AZ91D镁合金表面机械研磨处理的效果最好。
Objective To investigate the influence of surface mechanical attrition treatment technique on the grain refinement behavior and mechanism of AZ91D magnesium alloys. Methods The AZ91D magnesium alloy in hexagonal-closet-packet structure was treated by surface mechanical attrition treatment ( SMAT) with different ball diameters and handling time, and the microstruc-ture of surface deformed layer was characterized and compared. Results The grain of AZ91D magnesium alloys was obviously re-fined by surface mechanical attrition treatment. In a certain range, as the balls diameter or handling time increased, the grain size became smaller, and could finally reach about 24 nm. Conclusion The grain refinement mechanism of AZ91D magnesium alloy by surface mechanical attrition treatment was the results of twinning and dislocation slip. When the diameter of balls was 16 mm and the handling time was 180 min, surface mechanical attrition treatment has the highest efficiency.
参考文献
| [1] | MORDLIKE B L;EBERT T .Magnesium:Properties-applications- potential[J].Materials Science and Engineering A,2001,302(01):37-45. |
| [2] | 王亚鹏,孙凯.AZ91D镁合金表面改性层组织分析及其对耐蚀性影响的研究[J].表面技术,2010(03):60-62. |
| [3] | RODERT E;BROWN B .Magnesium Alloys and Their Applications International Conference[J].Light Metal Age,1998,56(7/8):94-99. |
| [4] | 王宾,叶宏,闫忠琳,邓代玉.镁合金表面铝涂层研究进展[J].表面技术,2010(01):85-88. |
| [5] | N. R. Tao;Z. B. Wang;W. P. Tong;M. L. Sui;J. Lu;K. Lu .An investigation of surface nanocrystallization mechanism in Fe induced by surface mechanical attrition treatment[J].Acta materialia,2002(18):4603-4616. |
| [6] | 田峰,杨辉.40Cr钢表面高能喷丸纳米化及其耐磨性能[J].表面技术,2013(05):52-54. |
| [7] | Tao Zhang;Dongpo Wang;Ying Wang;Caiyan Deng;Baoming Gong .Surface alloying method of ultrasonic shot peening on iron surface[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013(Jan.15):671-676. |
| [8] | 何晓梅,张聪惠,杨占林,刘晓燕,赵西成,于飞.退火对表面机械研磨处理纳米化工业纯钛性能的影响[J].金属热处理,2013(04):69-73. |
| [9] | Chen, A.Y.;Jia, Y.Q.;Pan, D.;Li, X.;Lu, J..Reinforcement of laser-welded stainless steels by surface mechanical attrition treatment[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2013:161-166. |
| [10] | 李玉荣,林万明,卫英慧,侯利锋,杜华云.表面机械研磨处理对Cu-10wt％Ni合金组织及性能的影响[J].功能材料,2011(z4):766-769. |
| [11] | 邹途祥,卫英慧,侯利锋,许并社,刘刚.纯铝表面机械研磨纳米化后的显微组织和硬度[J].机械工程材料,2009(01):40-43. |
| [12] | KLUG H P;ALEXANDER L E.X-ray Diffraction Proce-dures for Ploycrystalline and Amorphous Materials[M].New York:Wiley,1974 |
| [13] | 唐锋林 .表面纳米化处理对铝镁合金性能的影响[D].南宁:广西大学,2008. |
| [14] | 田志宏,张秀华,田志广.X射线衍射技术在材料分析中的应用[J].工程与试验,2009(03):40-42. |
| [15] | 侯利锋,卫英慧,刘宝胜,许并社.AZ31B镁合金表面纳米化处理后的显微结构特征[J].材料热处理学报,2007(z1):214-217. |
| [16] | 徐开东 .镁合金高能撞击表面纳米化与激光合金化研究[D].华中科技大学,2010. |
| [17] | 余琨,黎文献,王日初.镁合金塑性变形机制[J].中国有色金属学报,2005(07):1081-1086. |
| [18] | H.Q. Sun;Y.-N. Shi;M.-X. Zhang .Plastic strain-induced grain refinement in the nanometer scale in a Mg alloy[J].Acta materialia,2007(3):975-982. |
| [19] | 刘宝胜 .镁合金表面纳米化显微结构和晶粒细化机理研究[D].太原理工大学,2007. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%