目的：研究304不锈钢在模拟深海和浅海中的应力腐蚀开裂( SCC)行为。方法通过控制不同环境因素模拟南海某海域环境，利用动电位扫描、交流阻抗谱、慢应变速率拉伸( SSRT)及SEM表面分析等手段进行研究。结果304不锈钢在模拟海水溶液中呈现钝化状态，出现应力腐蚀敏感性，且裂纹扩展方式为穿晶开裂。在深海中的SCC机制为氢致开裂，浅海中的SCC机制主要为阳极溶解。结论304不锈钢在深海与浅海中的SCC机制不同，但两者的SCC敏感性相近且相对较低，在模拟海水环境中的应用不受海水深度限制。
ABSTRACT:Objective To study the stress corrosion cracking ( SCC) behavior of 304 stainless steel in simulated deep and shal-low seawater environments. Methods The environment of a sea area in the South Sea was simulated by controlling different environ-mental factors, and potentiodynamic polarization, electrochemical impedance spectroscopy, slow strain rate test ( SSRT) and super-ficial analysis technique using scanning electron microscope were applied for the research. Results 304 stainless steel exhibited a passivation behavior in the simulated seawater solution, and showed SCC susceptibility, besides, the crack propagation mode was transgranular cracking. The SCC mechanism in shallow sea was mainly controlled by anodic dissolution, while that in deep sea was controlled by hydrogen embrittlement. Conclusion Although 304 showed different SCC mechanisms in simulated deep sea and shal-low sea, the SCC sensitivities were close and relatively low. So the use of 304 SS in simulated seawater environment was not limited by the depth of seawater.
参考文献
| [1] | 黄桂桥 .不锈钢在海洋环境中的腐蚀[J].腐蚀与防护,1999,20(9):392-394. |
| [2] | Osama M. Alyousif;Rokuro Nishimura .The stress corrosion cracking behavior of austenitic stainless steels in boiling magnesium chloride solutions[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(7):3040-3051. |
| [3] | 许淳淳,张新生,胡钢.拉伸变形对304不锈钢应力腐蚀的影响[J].材料研究学报,2003(03):310-314. |
| [4] | 刘智勇,董超芳,李晓刚,王立贤,郅青,梁平.硫化氢环境下两种不锈钢的应力腐蚀开裂行为[J].北京科技大学学报,2009(03):318-323. |
| [5] | Tao Zhang;Yange Yang;Yawei Shao;Guozhe Meng;Fuhui Wang .A stochastic analysis of the effect of hydrostatic pressure on the pit corrosion of Fe-20Cr alloy[J].Electrochimica Acta,2009(15):3915-3922. |
| [6] | BLUNDY R F;SHREIR L L .The Effect of Pressure on the Permeation of Hydrogen through Steel[J].Corrosion Sci-ence,1977,17:509-527. |
| [7] | 孙飞龙 .X70钢在深海环境中的腐蚀规律和应力腐蚀敏感性研究[D].北京:北京科技大学,2013. |
| [8] | 孙海静,刘莉,李瑛.深海静水压力环境下低合金高强度钢腐蚀行为研究[J].电化学,2013(05):418-424. |
| [9] | BECCARIA A M;CASTELLO G .Influence of Hydrostatic Pressure on Pitting of Aluminium in Sea Water[J].British Corrosion Journal,1985,20(4):183-186. |
| [10] | Hosni Ezuber;A. El-Houd;F. El-Shawesh .A study on the corrosion behavior of aluminum alloys in sea water[J].Materials & design,2008(4):801-805. |
| [11] | 曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,2008 |
| [12] | 束德林;凤仪;陈九磅.工程材料力学性能[M].北京:机械工业出版社,2005 |
| [13] | 刘智勇,王长朋,杜翠薇,李晓刚.外加电位对X80管线钢在鹰潭土壤模拟溶液中应力腐蚀行为的影响[J].金属学报,2011(11):1434-1439. |
| [14] | 郝文魁,刘智勇,李晓刚,杜翠薇.16Mn钢及其热影响区在碱性硫化物环境中的应力腐蚀行为与机理[J].金属学报,2013(07):881-889. |
| [15] | X.S. Du;Y.J. Su;J.X. Li;L.J. Qiao;W.Y. Chu .Stress corrosion cracking of A537 steel in simulated marine environments[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012(Dec.):278-287. |
| [16] | BIRNBAUM H K;SOFRONIS P .Hydrogen-enhanced Loca-lized Plasticity a Mechanism for Hydrogenerated Fracture[J].Material Science and Engineering,1994,176:191-202. |
| [17] | 张亮,李晓刚,杜翠薇,刘智勇,梁平.X70管线钢在含CO2库尔勒土壤模拟溶液中的腐蚀行为[J].金属学报,2008(12):1439-1444. |
| [18] | Pan C.;Chu WY.;Li ZB.;Liang DT.;Su YJ.;Gao KW.;Qiao LJ. .Hydrogen embrittlement induced by atomic hydrogen and hydrogen-induced martensites in type 304L stainless steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):293-298. |
| [19] | 方智;吴荫顺;曹备 等.奥氏体304不锈钢在活化态下的应力腐蚀与马氏体相变[J].中国腐蚀与防护学报,1994,14(4):277-278. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%