目的：研究316 L不锈钢在碱性硫化物溶液中的应力腐蚀行为，为其在碱性环境中的适用性提供参考依据。方法采用动电位极化曲线、电化学阻抗( EIS)测量技术、慢应变速率拉伸试验( SSRT)、U形弯试样浸泡试验以及SEM腐蚀形貌分析方法。结果316 L不锈钢试样在碱性硫化物溶液中具有较低的应力腐蚀( SCC)敏感性，腐蚀机理主要为阳极溶解型，且SCC敏感性随着pH升高而降低。结论316L不锈钢试样在碱性NaCl/Na2 S溶液中虽然表现出应力腐蚀特征，但敏感性较低，适用于该实验模拟的碱性溶液中。
ABSTRACT:Objective To study the stress corrosion cracking (SCC) behavior of 316L stainless steel in alkaline sulphide solu-tion, and to provide reference for its applicability in alkaline environment. Methods Potentiodynamic polarization, electrochemical impedance spectrums ( EIS) , slow strain rate test( SSRT) , U type bending immersion test and superficial analysis technique using scanning electron microscope (SEM) were applied. Results 316L stainless steel had relatively low SCC susceptibility in alkaline sulphide solution, and the main corrosion mechanism was anodic dissolution ( AD) . The SCC susceptibility decreased with the in-crease of pH value. Conclusion Although 316L stainless steel showed features of stress corrosion in alkaline NaCl/Na2 S solution, the SCC sensitivity was low, so it was suitable for the simulated alkaline solution in the experiment.
参考文献
| [1] | FINSGAR M;JACKSON J .Application of Corrosion Inhibi-tors for Steels in Acidic Media for the Oil and Gas Industry:A Review[J].Corrosion Science,2014,86:17-41. |
| [2] | JAMES G S.Oil and Gas Corrosion Prevention：From Sur-face Facilities to Refineries[M].Elsevier Science,2014:39-66. |
| [3] | 廖芝文.原油注碱防腐技术在常减压装置中的应用[J].石化技术与应用,2007(05):437-441. |
| [4] | 卫四凤.加工高酸原油的常减压装置的防腐研究[J].石油化工技术与经济,2011(03):58-61. |
| [5] | 邱宏斌.奥氏体不锈钢输油管道焊缝的应力腐蚀失效分析[J].化工设备与管道,2011(04):68-72. |
| [6] | P. Marcus;V. Maurice;H.-H. Strehblow .Localized corrosion (pitting): A model of passivity breakdown including the role of the oxide layer nanostructure[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(9):2698-2704. |
| [7] | 董超芳,关矞心,程学群,刘飞华,李岩,任爱,李晓刚.pH值对高温高压水中304L不锈钢应力腐蚀开裂的影响[J].北京科技大学学报,2010(12):1569-1573. |
| [8] | Mottu N;Vayer M;Dudognon J;Erre R .Structure and composition effects on pitting corrosion resistance of austenitic stainless steel after molybdenum ion implantation[J].Surface & Coatings Technology,2005(7):2131-2136. |
| [9] | Effects of temperature on the oxide film properties of 304 stainless steel in high temperature lithium borate buffer solution[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(12):2840. |
| [10] | DING J H;ZHANG L;LU M X et al.The Electrochemical Behavior of 316L Austenitic Stainless Steel in Cl-Contai-ning Environment under Different H2 S Partial Pressures[J].Applied Surface Science,2014,289:33-41. |
| [11] | MENG G Z;LI Y;SHAO Y W.Effect of Cl-on the Properties of the Passive Films Formed on 316L Stainless Steel in Acidic Solution[J].Material Science Technology,2014(3):1-6. |
| [12] | BANAS J;LELEK-BORKOWSKA U;MAZURKIEWICZ B et al.Effect of CO2 and H2 S on the Composition and Stabili-ty of Passive Film on Iron Alloys in Geothermal Water[J].Electrochimica Acta,2007,52:5704-5714. |
| [13] | 张成玉,戴晟,余海洲,胡富仁,严沾谋.热处理对316L不锈钢组织和性能的影响[J].南方金属,2007(01):31-34. |
| [14] | IOFA Z A;BATRAKOV V V;CHO N B.Influence of Anion Absorption on the Action of Inhibitors on the Acid Corrosion of Iron and Cobalt[J].Electrochimica Acta,1964(6):1645. |
| [15] | A. Davoodi;M. Pakshir;M. Babaiee;G.R. Ebrahimi .A comparative H_2S corrosion study of 304L and 316L stainless steels in acidic media[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2011(1):399-408. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%