目的:揭示在70~95℃施镀温度范围,Ni-P合金镀层显微形貌的变化规律,并探讨表面形貌结构、合金硬度及耐蚀性能的相关性。方法以施镀温度为变量,通过化学沉积的方法制备Ni-P合金镀层。对镀层表面形貌进行表征,测试镀层硬度,并采用盐酸为腐蚀介质进行浸泡,以相对腐蚀速率表征镀层的耐蚀性。结果在70~95℃的施镀温度范围内,随着温度升高,镀层形貌先趋于致密和平整,而后表面粗化,镀层的硬度和耐蚀性均呈现先提高、后降低的趋势。最佳镀层形貌和硬度值出现在85℃,耐蚀性最好的施镀温度区间为85~90℃。结论当镀液pH值为4.5±0.1,施镀时间为3 h时,施镀的最佳温度为85℃。此条件下制备的镀层表面平整且均匀致密,硬度高,耐蚀性能优异。
ABSTRACT:Objective The variation trend of surface morphology of the Ni-P alloy coating was studied in the plating temperature range of 70~95 ℃. In addition, the correlations between alloy hardness, corrosion resistance and surface morphology were dis-cussed. Methods Ni-P alloy coatings were prepared by chemical deposition at different plating temperatures. The surface morpholo-gy of Ni-P coatings was characterized by SEM. The hardness of Ni-P coatings was determined. And the corrosion resistance of Ni-P coatings was also characterized by the relative corrosion rate through soaking the samples in chlorhydric acid. Results In the plat-ing temperature range of 70~95 ℃, with the increase of the deposition temperature, the surface morphology of Ni-P coatings ten-ded to be denser and smoother at first and then surface coarsening occurred. Both the hardness and corrosion resistance of the Ni-P coatings first increased and then decreased with the increasing deposition temperature. The best surface morphology and the maxi-mum hardness were obtained at 85 ℃ and the deposition temperature range for good corrosion resistance was 85~90 ℃. Conclu-sion The Ni-P coatings with flat, dense and smooth surface, high hardness and good corrosion resistance were prepared at 85℃ for 3 h when the solution pH value was 4. 5±0. 1.
参考文献
[1] | 祝文沙 .玻璃表面无钯活化及化学镀镍磷工艺研究[D].秦皇岛:燕山大学,2013. |
[2] | 刘宏,卞建胜,李莎,张彪.化学镀镍磷基合金镀层耐磨性的研究进展[J].表面技术,2012(04):91-94,98. |
[3] | 李东栋,王凤平.硫酸镍和碱式碳酸镍主盐对镁合金化学镀镍的影响[J].材料保护,2008(07):37-39,72. |
[4] | 姜东梅,赵金瑞,李雪松.pH值对AZ 91D镁合金化学镀镍的影响[J].电镀与环保,2008(02):26-28. |
[5] | 尚淑珍,路贵民,赵祖欣.沉积时间对镁合金表面化学镀镍磷合金的影响[J].表面技术,2009(06):73-75. |
[6] | 陈月华,刘永永,江德凤,袁礼华.化学镀镍施镀过程稳定性分析[J].表面技术,2013(02):74-76. |
[7] | 李国华,郝建民,陈永楠,陈宏.温度对AZ91D镁合金化学镀镍层结构和耐蚀性能的影响[J].铸造技术,2014(02):305-308. |
[8] | 包雨威 .细薄钢件表面化学镀工艺的研究[D].东华大学,2014. |
[9] | 尚淑珍,路贵民,赵祖欣,万以郡.沉积温度对AZ31镁合金镍磷合金镀层的影响[J].腐蚀与防护,2010(02):125-127. |
[10] | 朱焱,孔小雁,黄锦涛.Q235钢上中温化学镀镍磷合金工艺[J].电镀与涂饰,2011(05):21-24. |
[11] | 黄琳,徐想娥,汪万强.低温化学镀镍磷合金工艺[J].电镀与涂饰,2013(04):21-23. |
[12] | 龚妙毅.低温化学镀镍溶液及工艺条件的影响[J].科技创新与应用,2013(31):14-14. |
[13] | 苌清华,韩剑,支二辉,陈艳芳,杨秋菊.温度对镁合金表面化学镀Ni-P合金性能的影响[J].南方金属,2010(01):21-23,30. |
[14] | 王喜然,郭东海,张齐飞,王波波.工艺条件对碳钢表面化学镀Ni-P质量的影响[J].表面技术,2009(05):74-76. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%