目的：验证阴极保护系统在保护目标管道的同时对临近管道造成的杂散电流腐蚀,对比柔性阳极与阳极地床在保护管道的过程中产生的杂散电流污染情况,确定同沟铺设的不同管道联合保护方案。方法通过同一排流设备对相同区域的不同管线进行统一保护,阴极保护系统中的接地装置作为唯一的阳极,多条埋地管线作为电化学电池的阴极实现保护。结果阳极地床产生的杂散电流干扰明显强于柔性阳极材料；排流保护中,两条20 m埋地金属管道达到排流保护的范围时,柔性阳极的排流电压为1.2~1.52 V,远小于碳钢阳极地床的3.5~15 V,能够有效减少防护过程中电能的使用。结论同一阴极系统同时对多条金属管道或金属构筑物进行排流保护的措施可行。
ABSTRACT:Objective To verify the stray current corrosion caused to the adjacent pipelines by the cathodic protection system when protecting the target pipeline, compare the stray current pollution generated by flexible anode and anode ground bed during pipeline protection process, and propose joint protection of different pipelines buried in the same ditch. Methods The different pipelines in same region were jointly protected through the same drainage device, using the grounding device of the cathodic protec-tion system as the only anode, and the multiple buried pipelines as the cathode of the electrochemical cell. Results The stray cur-rent interference caused by the anode ground bed was obviously stronger than that of the flexible anode material. In drainage protec-tion, when the two 20 m buried metallic pipelines reached the range of drainage protection, the drainage voltage of the flexible an-
ode was 1. 2 V to 1. 52 V, which was far smaller than that of the carbon steel anode ground bed (3. 5~15 V), effectively reducing the power consumption during the protection process. Conclusion The drainage protection of multiple metallic pipelines or metallic structures using the same cathodic system was feasible.
参考文献
| [1] | 张攀峰,於孝春.受直流杂散电流影响埋地管线的ANSYS模拟[J].腐蚀与防护,2011(02):146-149. |
| [2] | L.Y.Xu;X. Su;Y.F.Cheng .Effect of alternating current on cathodic protection on pipelines[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2013(Jan.):263-268. |
| [3] | 景世刚 .金属管道防腐技术动向[J].表面技术,1998,27(1):28-29. |
| [4] | 刘金和,张雅琴,刘慕懿,胡喜艳,雍兴跃.有机涂层在模拟沙漠大气环境下的加速试验研究[J].表面技术,2014(4):64-67,96. |
| [5] | 米琪 .柔性聚合物阳极地床在阴极防腐蚀工程中的应用及发展[J].城市煤气,1993,l2:21-24. |
| [6] | El-Sayed A. Rassoul;Abdou Abdel-Samad;Rashad El-Naqier .On the cathodic protection of thermally insulated pipelines[J].Engineering failure analysis,2009(7):2047-2053. |
| [7] | 郭军科,于金山,彭翔,尹力,曹顺安.加速腐蚀实验研究碳钢的大气腐蚀行为[J].表面技术,2014(4):68-73. |
| [8] | Application of nickel-coated carbon fibre material in cathodic protection of underground-buried steel structures[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(11):2605. |
| [9] | ZhiGuang Chen;ChaoKui Qin;JiXu Tang.Experiment research of dynamic stray current interference on buried gas pipeline from urban rail transit[J].Journal of natural gas science and engineering,2013:76-81. |
| [10] | 赵晓云,陶文亮,李龙江,黄富惠,蒲明忠,刘起龙.国内外柔性阳极的开发应用现状及展望[J].腐蚀科学与防护技术,2013(05):437-441. |
| [11] | 周新荣,金永旺,于清涛,常庆海.浅谈阴极保护之柔性阳极的应用[J].中国石油和化工标准与质量,2013(14):60-61. |
| [12] | 滕延平,张丰,赵晋云,蒋国辉,隋溪,周兴涛,韩兴平.杂散电流干扰下管道密间隔电位检测数据处理方法[J].管道技术与设备,2009(04):29-31. |
| [13] | SAM A W.管线腐蚀控制[M].北京:化学工业出版社,2004 |
| [14] | 李龙江,陶文亮.酸湿土壤中燃气管道阳极保护的研究与实现[J].煤气与热力,2011(12):71-75. |
| [15] | 熊娟,郑兴文,张文艳,范金龙,黄恩龙.西南地区某输油管道外腐蚀分析[J].表面技术,2014(4):59-63,157. |
| [16] | 龚敏,张婷,熊娟,郑兴文,林修洲,侯胜.油气运输管道防腐层的抗阴极剥离性能[J].表面技术,2012(01):30-32,47. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%