目的：研究钼酸钠、葡萄糖酸钠及其复配物在氯化钠介质中,对304不锈钢点蚀的缓蚀作用。方法对钼酸钠、葡萄糖酸钠按不同配比进行复配得到不同缓蚀剂,采用极化曲线法分别测试在这几种缓蚀剂存在的条件下,304不锈钢在3.5%(质量分数,后同) NaCl溶液中的点蚀电位。结果单组分的钼酸钠、葡萄糖酸钠对在3.5%NaCl介质中的304不锈钢点蚀有一定的抑制作用,且两种缓蚀剂有明显的协同缓蚀效应。结论当复配缓蚀剂配比为c(钼酸钠)∶c(葡萄糖酸钠)=2∶1时,其缓蚀效果达到最佳,点蚀电位为436 mV。
ABSTRACT:Objective To investigate the inhibition effect of sodium molybdate, sodium gluconaten and their mixtures on 304 stainless steel in sodium chloride medium. Methods Sodium molybdate and sodium gluconate were compounded at different propor-tions to obtain different complex inhibitors, and then electrochemical polarization curve was used to test the pitting potential of 304 stainless steel in 3. 5% NaCl solution in the presence of these types of corrosion inhibitors. Results One-component sodium molyb-date and sodium gluconate exhibited certain inhibitory effects for pitting on 304 stainless steel in 3. 5% NaCl medium, and there was significant synergistic inhibition effect between these two corrosion inhibitors. Conclusion The best ratio of the compounded in-hibitor was 2∶1 (27 mmol/L sodium molybdate and 13 mmol/L sodium gluconaten), and the pitting potential could reach 436 mV.
参考文献
| [1] | 张欢 .氯化钠介质中06Cr19Ni10 不锈钢缓蚀剂的研制[D].武汉:机械科学研究总院武汉材料保护研究所,2009. |
| [2] | 张欢,余静,徐燕飞,黄业荣,顾卡丽,杨昊.4种环境友好型缓蚀剂对304不锈钢在氯化钠介质中点蚀的抑制作用[J].材料保护,2010(06):72-74. |
| [3] | KOLTS J H;DELZER G A .Enhanced Ethylene and Ethane Production with Free-radical Cracking Catalysts[J].Sci-ence,1986,232(4751):744-746. |
| [4] | 芮玉兰,于静敏,路迈西,梁英华,田会娟.盐酸体系不锈钢缓蚀剂的开发[J].腐蚀与防护,2007(03):109-112,115. |
| [5] | FENG Y;SIOWA K S;TEO W K et al.The Synergistic Effects of Propargyl Alcohol and Potassium Iodide on the In-hibition of Mild Steel in 0. 5M Sulfuric Acid Solution[J].Corrosion Science,1999,41:829-852. |
| [6] | 龚洵洁,李宇春,彭珂如,谢学军.钼酸盐缓蚀剂在自来水中的缓蚀机理研究[J].腐蚀科学与防护技术,2001(04):208-210. |
| [7] | 安洋,徐强,任志峰,唐致远.工业循环冷却水中不锈钢点蚀缓蚀剂的研究[J].电镀与精饰,2011(07):1-4,41. |
| [8] | 孙彩霞,徐会武,陈燕敏,陈敏,刘荣江,程玉山.复合型钼酸盐缓蚀剂性能研究[J].应用化工,2013(09):1608-1610,1613. |
| [9] | ILEVBARE G O;BURSTEIN G T .The Inhibition of Pitting Corrosion of Stainless Steels by Chromate and Molybdate Ions[J].Corrosion Science,2003,45:1545-1569. |
| [10] | 李玉明,刘静敏,马志超,匡云飞.钼酸盐与磷酸盐、硅酸盐复配缓蚀剂的研究[J].腐蚀与防护,2004(06):248-251. |
| [11] | 杨群英 .电化学方法评价缓蚀剂性能的可行性研究[D].西安石油大学,2009. |
| [12] | 余国骏,汤兵.缓蚀剂研究中的电化学方法[J].中国腐蚀与防护学报,2009(01):76-80. |
| [13] | 陈旭俊;王海林;陈振家 .钼酸盐对不锈钢孔蚀抑制作用机理的研究[J].中国腐蚀与防护学报,1992,12(3):214-219. |
| [14] | 杨仁春 .钼酸盐缓蚀剂对A20碳钢缓蚀机理与协同效应的研究[D].新疆大学,2007. |
| [15] | 宋蔚,田禾,张津红.缓蚀剂的成膜机理分析[J].天津理工学院学报,2004(04):67-70. |
| [16] | 汪的华.缓蚀剂吸附行为研究进展与展望[J].材料保护,2000(01):29-32. |
| [17] | 第五方 .不锈钢表面复合型缓蚀剂的研究[D].西安电子科技大学,2009. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%