目的：制备具有优良自润滑性能的Ni-PTFE复合镀层,同时探究其摩擦学性能。方法首先在铜基体表面电泳沉积一层PTFE膜,再将覆有PTFE膜的基体放入光亮镀镍溶液中进行电沉积(电泳-电沉积法),用SEM附带的能谱仪检测复合镀层的PTFE复合量,同时在自制的销盘摩擦磨损实验机上进行相关的摩擦学实验,以评价其摩擦学性能。结果用电泳-电沉积法制备出了含量(以体积分数计)达63.4%的Ni-PTFE复合镀层。在干摩擦条件下,PTFE微粒的加入可以降低复合镀层的摩擦系数(最低至0.067)。结论高PTFE复合量的复合镀层具有良好的耐磨性能。
Objective To prepare Ni-PTFE composite coatings with excellent self-lubricating property, and to explore its tribo-logical performance. Methods First, a layer of PTFE membrane was deposited on the surface of the copper matrix by electrophoret-ic deposition, and then the matrix with a layer of PTFE membrane was put into the bright nickel plating solution for electrodeposi-tion ( electrophoresis-electrodeposition method) . SEM with EDS was used to detect the PTFE contents of the composite coating. At the same time, related tribological experiments were conducted on a self-developed pin disk friction tester, so as to evaluate its tri-bological performance. Results Using the electrophoresis-electrodeposition method, composite coatings with 63. 4% Ni-PTFE were prepared. The addition of PTFE particles could decrease the friction coefficient of the composite coating (minimum 0. 067) under dry friction condition. Conclusion The composite coating with high content of PTFE had good wear resistance.
参考文献
| [1] | 鸿建.化学工业电镀工艺学[M].哈尔滨:哈尔滨工业大学出版社,1988 |
| [2] | 刘国钦;陈观雄;韩斌 .镍-金刚石复合电镀的研究[J].表面技术,1991,20(03):18-22. |
| [3] | 茂忠.电镀理论与技术[M].哈尔滨:哈尔滨工业大学出版社,2004 |
| [4] | 温诗铸;黄平.摩擦学原理[M].北京:清华大学出版社,2002 |
| [5] | 邢声远;江锡夏;文永奋.纺织新材料及其识别[M].北京:中国纺织出版社,2002 |
| [6] | 程立新;邱建伟;杨杰辉 .Ni-PTFE复合镀层的性能及其新的应用[J].表面技术,1997,26(04):35-36. |
| [7] | 熊涛.化学镀Ni-P-PTFE复合镀层的研究进展[J].腐蚀与防护,2010(08):636-638,648. |
| [8] | 张会广 .双层Ni-P镀层及Ni-P/PTFE复合镀层的制备及性能研究[D].西南交通大学,2010. |
| [9] | 杨俊涛 .Ni-PTFE/Sn-Ni-PTFE自润滑复合镀层的制备工艺和性能研究[D].哈尔滨工程大学,2013. |
| [10] | 唐宏科,赵文轸.表面活性剂对Ni-Co-PTFE复合电镀的影响[J].宇航材料工艺,2006(03):47-50. |
| [11] | 李卫红 .自动电刷镀Ni-PTFE复合镀层特性及共沉积机制研究[D].上海交通大学,2008. |
| [12] | Shrestha NK.;Masuko M.;Saji T.;Sakurada K. .Composite coatings of nickel and ceramic particles prepared in two steps[J].Surface & Coatings Technology,2001(2):175-181. |
| [13] | 田海燕 .电泳-电沉积镍基纳米复合镀层及其性能的基础研究[D].南京航空航天大学,2008. |
| [14] | 赵运伟,黄巍,田海燕,王晓雷.电泳-电沉积Ni-金刚石复合镀层及其耐磨性能研究[J].表面技术,2013(02):77-79,125. |
| [15] | Wei Huang;Yunwei Zhao;Xiaolei Wang.Preparing a high-particle-content Ni/diamond composite coating with strong abrasive ability[J].Surface & Coatings Technology,2013:489-494. |
| [16] | 付传起,王宙,何旭.Ni-P-PTFE复合镀层工艺及摩擦学行为研究[J].润滑与密封,2011(05):44-47. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%