目的 提高316 L不锈钢表面的光催化和亲水性能.方法 通过等离子表面合金化技术在316 L不锈钢表面制备结合良好的TiN薄膜,然后对TiN薄膜进行热氧化,得到N掺杂TiO2薄膜.利用X射线衍射仪、X射线光电子能谱仪、扫描电子显微镜及紫外-可见分光光度仪对制备的N掺杂TiO2薄膜进行表征,并通过光催化实验和亲水性实验考察其光催化性能和亲水性.结果 经过空气中450℃氧化处理2 h的薄膜中存在锐钛矿晶型的TiO2,样品中的N元素取代了部分O.未掺杂TiO2和N掺杂TiO2的带隙宽度分别为3.25、3.08 eV.经热氧化处理后,薄膜表面致密,无裂纹和微孔,均匀分布着尺寸相近的微小凸起物.经可见光照射150 min后,N掺杂TiO2薄膜对亚甲基蓝溶液的最终降解率为20%.此外,N掺杂TiO2薄膜具有较高的亲水性,可见光照射下,30min内接触角降为8.5°.结论 N掺杂TiO2薄膜能有效提高316 L不锈钢表面的光催化和亲水性能.
Objective To improve the photocatalytic and hydrophilic properties of 316L stainless steel surface. Methods N doped TiO2 thin films were obtained by thermal oxidation of titanium nitride films, which were prepared by plasma surface alloying on stainless steel substrate. The resultant thin films were characterized by X-ray diffraction ( XRD) , X-ray photoelectron spectros-copy ( XPS) , scanning electron microscopy ( SEM) , and ultra violet-visible absorption spectroscopy ( UV-Vis) methods. The pho-tocatalytic properties and hydrophilicity of N doped TiO2 thin films were studied through photocatalysis and hydrophilicity tests. Results XRD patterns showed that anatase type TiO2 existed in the thin films after thermal oxidation at 450 ℃ in air for 2 h. Ac-cording to XPS, residual N atoms partially occupied O atom sites in the TiO2 lattice. The band-gaps of TiO2 and N-doped TiO2 were 3. 25 eV and 3. 08 eV, respectively. A uniform and dense surface containing three-dimensional homogenous protuberances growth of grains was observed in SEM images of thin films after thermal oxidation. The experimental results of degradation of Methylene blue solution under visible light indicated that photocatalysis efficiency of N doped TiO2 film was better than that of the undoped film. The ultimate degradation rate of N doped TiO2 was 20% in visible irradiation for 150 min. The N doped TiO2 films showed a higher hydrophilicity and the contact angle was lowered to 8. 5° by Vis-irradiation within 30 min. Conclusion The N doped TiO2 film could effectively improve the photocatalytic and hydrophilic properties of stainless steel surface.
参考文献
| [1] | 李红伟;李雯;付涛;杨水云.低模量钛合金表面水热法制备含银二氧化钛抗菌薄膜[J].表面技术,2015(9):50-55. |
| [2] | 任达森;崔晓莉;张群;沃松涛;杨锡良;章壮健;陆明.溶胶法制备的二氧化硅与二氧化钛复合薄膜的性能[J].物理化学学报,2003(9):829-833. |
| [3] | 温久然;刘开平;孙志华;刘存强.TiO2/SiO2复合薄膜对玻璃亲水性的影响[J].表面技术,2014(1):90-94,118. |
| [4] | Christian Lettmann;Knut Hildenbrand;Wilhelm F.Maier;Horst Kisch;W.Macyk.Visible light photodegradation of 4-chlorophenol with a coke-containign titanium dioxide photocatalyst[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,20014(4):215-227. |
| [5] | Wei Zhao;Wanhong Ma;Chuncheng Chen;Jincai Zhao;Zhigang Shuai.Efficient Degradation of Toxic Organic Pollutants with Ni_2O_3/TiO_(2-x)B_x under Visible Irradiation[J].Journal of the American Chemical Society,200415(15):4782-4783. |
| [6] | Wan L;Li JF;Feng JY;Sun W;Mao ZQ.Improved optical response and photocatalysis for N-doped titanium oxide (TiO2) films prepared by oxidation of TiN[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,200710(10):4764-4767. |
| [7] | Lei Zhao;Qing Jiang;Jianshe Lian.Visible-light Photocatalytic Activity Of Nitrogen-doped Tio_2 Thin Film Prepared By Pulsed Laser Deposition[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,200815(15):4620-4625. |
| [8] | Hiroshi Irie;Yuka Watanabe;Kazuhito Hashimoto.Nitrogen-Concentration Dependence on Photocatalytic Activity of TiO_(2-x)N_x Powders[J].The journal of physical chemistry, B. Condensed matter, materials, surfaces, interfaces & biophysical,200323(23):5483-5486. |
| [9] | Cui X;Ma M;Zhang W;Yang YC;Zhang ZJ.Nitrogen-doped TiO2 from TiN and its visible light photoelectrochemical properties[J].Electrochemistry communications,20083(3):367-371. |
| [10] | Chen XB;Lou YB;Samia ACS;Burda C;Gole JL.Formation of oxynitride as the photocatalytic enhancing site in nitrogen-doped titania nanocatalysts: Comparison to a commercial nanopowder[J].Advanced functional materials,20051(1):41-49. |
| [11] | Cong Y;Zhang JL;Chen F;Anpo M.Synthesis and characterization of nitrogen-doped TiO2 nanophotocatalyst with high visible light activity[J].The journal of physical chemistry, C. Nanomaterials and interfaces,200719(19):6976-6982. |
| [12] | Akira Fujishima;Tata N. Rao;Donald A. Tryk.Titanium dioxide photocatalysis[J].Journal of photochemistry and photobiology, C. Photochemistry reviews,20001(1):1-21. |
| [13] | 汪宇炎;汪洋.TiO2薄膜在玻璃材料上的亲水性研究[J].表面技术,2009(2):52-54. |
| [14] | 黄东升;曾人杰;陈朝凤;李玉花.铁、氦共掺杂二氧化钛薄膜的亲水性能[J].物理化学学报,2007(7):1037-1041. |
| [15] | 余志勇;张维;马明;崔晓莉.阳极氧化TiN薄膜制备N掺杂纳米TiO2薄膜及其可见光活性[J].物理化学学报,2009(1):35-40. |
| [16] | 梅乐夫;梁开明.氮掺杂TiO2-ZrO2复合光催化薄膜的研究[J].稀有金属材料与工程,2008(5):758-761. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%