目的：研究长输管线压缩机叶片材料FV(520)B不锈钢在高含H2S、H2O、CO2条件下的腐蚀行为。方法利用高温高压反应釜模拟特定工况，在H2S分压为0.9 MPa、CO2分压为0.6 MPa、温度为150℃的条件下于5 g/L的氯化钠溶液中制备硫化腐蚀层，利用XPS、SEM、XRD等手段对腐蚀层的成分及结构进行分析。结果 FV(520)B不锈钢的腐蚀速率逐渐降低，试样表面粗糙度先增大后下降，腐蚀产物主要为FeCO3、Fe3O4、FeS、FeS2、S、Cr2S3、Cr2O3和Cr(OH)3。结论在腐蚀前期，FeS的形成速率大于 FeS2、S，腐蚀产物颗粒不断长大。形成完整的 Cr2O3、Cr(OH)3保护膜后，腐蚀得到抑制，此时腐蚀反应主要为FeS2、S的生成，试样表面腐蚀产物颗粒尺寸变小，试样表面粗糙度降低。
ABSTRACT:Objective To study the corrosion behavior of the blade material FV(520)B stainless steel of long pipeline com-pressor under special working conditions containing high H2S, H2O and CO2.Methods A high temperature and high pressure reaction kettle was used to simulate the specific working conditions. FV(520)B specimen was put in 5 g/L NaCl solution to pre-pare the sulfidation corrosion layer, the temperature was 150℃, the H2S partial pressure was 0.9 MPa and the CO2 partial pressure was 0.6 MPa. XPS, SEM and XRD were applied to investigate the composition and structure of the corrosion layer. Results When FV(520)B stainless steel was corroded under the above conditions, the corrosion rate gradually decreased, the surface roughness of the sample first increased and then decreased. The components of corrosion products were mainly FeCO3, Fe3O4, FeS, FeS2, S, Fe3O4, Cr2S3, Cr2O3 and Cr(OH)3. Conclusion In the early stage of corrosion, the formation rate of FeS was higher than those of FeS2 and S, and the corrosion products were growing up. In the late period of corrosion, because the com-plete protection film of Cr2O3and Cr(OH)3 was formed, the corrosion was inhibited and the main reaction was the formation of FeS2 and S. The particle size of the corrosion products on the surface of the sample and the roughness were both reduced.
参考文献
| [1] | 刘智勇;董超芳;李晓刚;王立贤;梁平.35CrMo和00Cr13Ni5Mo硫化氢环境应力腐蚀开裂[J].化工学报,2008(10):2561-2567. |
| [2] | 曹耀峰.高酸性气田开发安全工程概论--普光气田安全工程实践[J].中国工程科学,2010(10):9-13. |
| [3] | 燕铸;钱进森;李振东;刘建彬;李小波.油管钢在高温高压H2S/CO2环境中的二次腐蚀行为研究[J].焊管,2014(10):20-25. |
| [4] | 赵永峰 .13Cr钢在CO<,2>-H<,2>S-Cl<'->体系中的腐蚀行为及其缓蚀技术研究[D].北京化工大学,2010. |
| [5] | 李自力;程远鹏;毕海胜;董有智.油气田CO2/H2S共存腐蚀与缓蚀技术研究进展[J].化工学报,2014(2):406-414. |
| [6] | Jiabin Han;David Young;Hendrik Colijn.Chemistry and Structure of the Passive Film on Mild Steel in CO2 Corrosion Environments[J].Industrial & Engineering Chemistry Research,200913(13):6296-6302. |
| [7] | 闫伟;邓金根;董星亮;张春阳;李立宏;李晓蓉.油管钢在C02/H2S环境中的腐蚀产物及腐蚀行为[J].腐蚀与防护,2011(3):193-196. |
| [8] | 吕祥鸿;赵国仙;张建兵;谢凯意.超级13Cr马氏体不锈钢在CO_2 及H_2 S/CO_2 环境中的腐蚀行为[J].北京科技大学学报,2010(2):207-212. |
| [9] | 杨怀玉;曹殿珍;陈家坚;祝英剑;时维才;钱家煌;郭文斌.CO2饱和溶液中缓蚀剂的电化学行为及缓蚀性能[J].腐蚀科学与防护技术,2000(4):211-214. |
| [10] | 伍丹丹;肖琪;王树涛;黄雪松;关建庆;张庆生.抗硫套管钢P110SS在高含H2S/CO2、Cl-共存条件下的腐蚀行为[J].腐蚀与防护,2014(2):112-115. |
| [11] | 李党国;冯耀荣;白真权;郑茂盛.Cl-对N80钢在CO2水溶液中腐蚀行为的影响[J].腐蚀科学与防护技术,2007(5):329-332. |
| [12] | 赵平;安成强.H2S腐蚀的影响因素（Ⅰ）[J].全面腐蚀控制,2002(2):5-6,29. |
| [13] | 李萍.90℃时油管钢P110的CO2/H2S腐蚀行为[J].全面腐蚀控制,2006(02):18-19,23. |
| [14] | 王斌;李春褔;范舟;陈玉祥.合金元素和控制轧制对低合金高强度钢抗硫化氢腐蚀的影响[J].腐蚀与防护,2005(9):402-406. |
| [15] | 邓洪达;崔世华;李春福;曹献龙;兰伟.镍基合金G3在高含H2S和CO2环境中的腐蚀行为[J].腐蚀与防护,2013(4):302-306. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%