通过旋转失重实验研究了两种σ相强化的候选材料S1,S2和作为对比的316L在10%H2SO4+15%刚玉砂介质中的冲刷与腐蚀的交互作用规律及其与耐冲刷腐蚀合金设计的关系.结果表明,低含量、小尺寸的σ相对S1钢(Cr25-Ni25-Mo5)耐蚀性的影响不明显,仅能提高其低流速条件下的抗冲刷性能.相反,高含量、大尺寸的σ相能显著提高S2钢(Cr30-Ni22-Mo3)在各种流速条件下的抗冲刷性,从而导致其交互作用和总失重率显著降低,尽管其耐蚀性相对很差.冲刷和腐蚀交互作用失重率是冲刷腐蚀总失重率的良好表征.寻求耐蚀性与耐冲刷性能间的最佳平衡以使交互作用量最小,是发展抗冲刷腐蚀材料的最佳途径.
参考文献
| [1] | Madsen B W. Wear, 1989; 134:59 |
| [2] | Ma N H, Rao Q C, Zhou Q D. Wear, 1989; 132:347 |
| [3] | Li J L, Tang J L. Wear, 1990; 138:23 |
| [4] | Shinogaya T, Yamamoto H, Wasaka S, Ishizuka M. Kagaku Kogaku, 1990; 54:65 |
| [5] | Chakraborty I, Basak A, Chatterjee U K. Wear, 1991; 143:203 |
| [6] | Fishman V. International Conference on Advances in Corrosion and Protection, Paper No.415, June 28th-July 3rd,1992, UMIST, Manchester, UK |
| [7] | Li S Z, Jiang X X. Corros Sci Protect Techniq, 1995; 7:122(李诗卓,姜晓霞.腐蚀科学与防护技术,1995;7:122) |
| [8] | Zhang Y S, Wei X Y, Zhang Y D. Report on F7 Alloy. Institute of Corrosion and Protection of Metals, The Chinese Academy of Sciences, 1992(张玉生,魏翔云,张雅东.F7合金鉴定材料.中国科学院金属腐蚀与防护研究所内部资料,1992) |
| [9] | Potgieter J H. Br Corros J, 1992; 27:219 |
| [10] | Zheng Y G, Yao Z M, Long K, Li S C, Ke W. Corros Sci Protect Techniq, 1993; 5:286(郑玉贵,姚治铭,龙康,李生春,柯伟.腐蚀科学与防护技术,1993;5:286) |
| [11] | Yao Z M, Zheng Y G, Ke W. Wear, 1995; 186-187:568 |
| [12] | Wei X Y, Zheng Y G, Zhang Y S, Yao Z M, Zhang Y D,Zhang S P, Ke W. Acta Metall Sin, 1994; 30:A91(魏翔云,郑玉贵,张玉生,姚治铭,张亚东,张绍鹏,柯伟.金属学报,1994;30:A91) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%