研究了一种等温锻造态Ti-47Al-1Cr-1V-1.5Mo-1.5Nb(原子分数,%)合金的超塑变形行为和组织变化.结果表明:在900℃,·ε=5×10-4s-1和大气条件下,合金的应变速率敏感性指数m大于0.5,延伸率为200%.超塑变形时,在γ相晶内、晶界和层状组织中发生了动态再结晶.动态再结晶可松弛界面滑动造成的应力集中,也为合金进一步的超塑变形创造了组织条件.γ晶粒中发生{111}1/2〈110]普通位错滑移、{111}〈101]超点阵位错滑移和{111}〈112]类型孪生变形.位错滑移和孪生既对变形做出贡献,同时也作为调节机制起作用.
参考文献
| [1] | Cheng S C, Wolfenstine J, Sherby O D. Metall Trans, 1992;23A: 1509 |
| [2] | Imayev R M, Imayev V M, Salishev G A. J Mater Sci, 1992;27:4465 |
| [3] | Lee W B, Yang H S, Kim Y W, Mukherjee A K. Scr Metall Mater, 1993; 29:1403 |
| [4] | Wajata T, Isonish K, Ameyama K, Tokizane M. ISIJ Int,1993; 33:884 |
| [5] | Lee W B, Yang H S, Mukherjee A K. Mater Sci Eng, 1995;A192/193:733 |
| [6] | Vanderschuren D, Nobuki M, Nakamura M. Scr Metall Mater, 1993; 28:605 |
| [7] | Nieh J G, Wadsworth J. Mater Sci Eng, 1997; A239/240:88 |
| [8] | Huang B Y, He Y H, Deng Z Y, Wang J N, Sun J. Acta Metall Sin, 1998; 34:1173(黄伯云,贺跃辉,邓忠勇,王健农,孙坚.金属学报,1998;34:1173 |
| [9] | Zhou K C, Huang B Y, Qu X H, Chen X Q. Rare Metal Mater Eng, 1998; 27:336(周科朝,黄伯云,曲选辉,陈小群.稀有金属材料与工程,1998;27:336) |
| [10] | Shi X H, Zhang D, Ge Y, Qin J N, Zhang G D. Mater Sci Eng, 1998; 16:24(施幸华,张荻,葛云,覃继宁,张国定.材料科学与工程,1998;16:24) |
| [11] | Zhang D, Qin J N, Shi X H , Zhang G D. Rare Metal Mater Eng, 1998; 27:210(张荻,覃继宁,施幸华,张国定.稀有金属材料与工程,1998;27:210) |
| [12] | Yamaguchi M, Umakoshi Y eds., Ding S S trans. Intermetallics. Beijing: Sciences press, 1999:40(山口正治,马越佑吉著,丁树深译.金属间化合物.北京:科学出版社,1991:40) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%