对Ml(Ni4.55-xCoxMn0.4Ti0.05)合金(x=0.0-0.8)的相结构、气态吸放氢特性及电化学性能进行了系统的研究.结果表明,在x ≤0.3的组成范围内,合金保持单一的LaNi5相;当x＞0.3时,合金中析出多种第二相,且第二相总量随Co含量的增加而增多.随合金Co含量的增加,晶胞体积增大,吸放氢平台下降,滞后减小,但贮氢容量降低.在x≤0.3的组成范围内,合金的Co含量增加提高了合金的放电容量和高倍率放电性能;当x＞0.3时,合金的放电容量下降,但改善了合金的循环稳定性.
参考文献
| [1] | Lei Y Q, Li Z P, Chen C P, Wu J, Wang Q D. J LessCommon Met, 1991; 172:1265 |
| [2] | Sakai T, Yoshinaga H, Miyamura H, Kuriyama N,Ishikawa H. J Alloys Compd, 1992; 180:37 |
| [3] | Jiang J J, Lei Y Q, Sun D L, Wang C S, Wu J, Wang Q D. Acta Metall Sin, 1995; 31:B379(江建军,雷永泉,孙大林,王春生,吴京,王启东.金属学报,1995;31:B379) |
| [4] | Chartouni D, Meli F, Zuttel A, Gross K, Schlapbach L. J Alloys Compd, 1996; 241:160 |
| [5] | Iwakura C, Fukuda K, Senoh H, Inoue H, Matsuoka M,Yamamoto Y. Electrochim Acta, 1998; 43:2041 |
| [6] | Analysis center of Generator Corporation. The Manual of X-Ray Diffraction. Tokyo: NTS, 1987:236(理学电机株式会社分析中心编.X射线衍射手册.东京:NTS出版社,1987:236) |
| [7] | Brewer L, Wengert P R. Metall Trans, 1973; 4:83 |
| [8] | Alefeld G, Volkl J. Hydrogen in Metals Ⅱ: Application-Oriented Properties, New York: Springer-Verlag, 1978:227 |
| [9] | Oesterreicher H, Cliton J, Bittner H. Mater Res Bull,1976; 11:1241 |
| [10] | Sakai T, Oguro K, Miyamura H, Kuriyama N, Kato A,Ishikawa H, Iwakura C. J Less-Common Met, 1990; 161:127 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%