研究了Ni,Ni-5Ti,Ni-10Ti及Ni-15Ti(质量分数,%,下同)合金在650℃熔融(62Li-38K)2CO3(摩尔分数,%)中,空气气氛下的腐蚀行为.Ni-5Ti合金的腐蚀速度小于纯镍,表面形成Ni和Ti的混合氧化膜,Ni-10Ti和Ni-15Ti合金的腐蚀速度却明显高于纯镍,表面也形成了Ni和Ti的混合氧化膜,但沿原始合金中的TiNi3相发生了严重的Ti的内氧化.和纯镍相比,Ni-Ti合金表面氧化膜的生长速度明显减慢,讨论了合金腐蚀机制.
参考文献
| [1] | Plomp L, Veldhuis J B J. J Power Sources, 1992; 39(3):369 |
| [2] | Makkus R C, Hemmes K, Wit J H. J Electrochem Soc,1994; 141(12): 3429 |
| [3] | Pierce R D, Smith J L, Kucera G H. In: Selman J R,Shores D A, Maru H C, Uchida Ieds, Proceedings of the Second Symposium on Molten Carbonate Fuel Cell Technology, Pennington, NJ, 1990; PV90-16:226 |
| [4] | Ota K I, Takeishi Y, Shibata S, Yoshitake H, Kamiya N,Yamazaki N. J Electrochem Soc, 1995; 142:3322 |
| [5] | Yang B Y, Kim K Y. Electrochim Acta, 1998; 43(21-22):3343 |
| [6] | Chauvaut V, Cassir M, Denos Y. Electrochim Acta, 1998;43:1991 |
| [7] | Kofstad P. J Less-Common Met, 1967; 12:449 |
| [8] | Wahlbeck P G, Gilles P W. J Am Ceram Soc, 1966; 49:180 |
| [9] | Gesmundo F, Niu Y, Viani F, Rizzo F C. Oxid Met, 1996;46:441 |
| [10] | Stott F H, Wood G C. Mater Sci Technol, 1988; 4:1072 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%