研究了经峰时效(T5)及过时效(T5+300℃)处理的莫莱石短纤维增强ZL107复合材料在300℃时的拉-拉循环蠕变的行为.实验结果表明:两种热处理状态下,复合材料都显示出循环蠕变减速现象.峰时效状态下,循环蠕变与静态蠕变相比表现出低的表观激活能,非热空位机制作用较大;而过时效状态下,循环蠕变与静态蠕变相比表现出高的表观激活能,滞弹性机制作用较大.
参考文献
| [1] | Fan J Z,Yao Z K,Li Y C.Mater Rev,1997;11(3):48(樊建中,姚忠凯,李义春.材料导报,1997;11(3):48) |
| [2] | Cade K J, Pahutova M. Mater Sci Eng, 1994; A20(1): 141 |
| [3] | Li Y, Mohamed F A. Acta Mater, 1997; 45(11): 4775 |
| [4] | Liu P L, Wang G Z, Wang W L, Toda H, Kobayashi T.Acta Metall Sin, 1997; 33(11): 1227(刘丕林,王光中,王文龙,户田裕之,小林俊郎.金属学报,1997;33(11):1227) |
| [5] | Dlouhy A, Merk N, Eggeler G. Acta Metall Mater, 1993;41:3245 |
| [6] | Krajewski P E, Allison J E, Jones J W. Metall Trans,1993; A24:2731 |
| [7] | Nardone V C, Kimmerle W L, Tien J K. Metall Trans,1986; A17:1577 |
| [8] | Stefani J A, Nardone V C, Tien J K. Scr Metall, 1987; 21:1 |
| [9] | Liu P L, Wang G Z, Wang W L. Mater Sci Tech, 1997;13:667 |
| [10] | Liu P L, Wang G Z, Toda H, Kobayashi T. Scr Metall,1997; 36:807 |
| [11] | Chen R, Zhao P, Dong B, Gao S J, Shen B L, Tu M J.Chin J Non-Met, 1998; 8(1): 181(陈睿,赵平,董斌,高升吉,沈保罗,涂明旌.中国有色金属学报,1998;8(1):181) |
| [12] | Vyletel G M, Aken D C. Mater Trans, 1995; A26:3155 |
| [13] | Stefano S, Lorenzo P. Metall Mater Trans, 1995; A26:2745 |
| [14] | Shrikant P, Bhat Campbell L. Acta Metall, 1979; 27:1861 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%