利用作者自行开发和改良的Monte Carlo计算机仿真算法,对含不同数量第二相粒子的虚拟材料基体中三维晶粒长大过程的影响进行了仿真和定量分析结果表明,随粒子体积分数增加,晶粒长大指数下降,停滞状态的晶粒尺寸分布宽度减小.通过计算机仿真获得了极限晶粒尺寸和粒子参量间的定量关系,并由几何模型给出了证明.与文献中已有理论模型、计算机仿真及实验结果进行的比较分析表明,本文所得结果与实测结果符合得更好.
参考文献
[1] | Zener C. Trans AIME, 1948; 175:15 |
[2] | Hillert M. Acta Metall, 1965; 13:227 |
[3] | Gladman T. Proc R Soc A, London, 1966; 294:298 |
[4] | Hellman P, Hillert M. Scandinavian. J Metall, 1975; 4:211 |
[5] | Hillert M. Acta Metall, 1988; 36:3177 |
[6] | Hunderi O, Ryum N. Acta Metall Mater, 1992; 40:543 |
[7] | Anand L, Gurland J. Metall Trans, 1975; 6A: 928 |
[8] | Tweed C J, Hansen N, Ralph B. Metall Trans, 1983; 14A:2235 |
[9] | Olgaard D L, Evans B. J Am Ceram Soc, 1986; 69C: 272 |
[10] | Srolovitz D J, Grest G S, Sahni P S. Acta Metall, 1984;32:1429 |
[11] | Doherty R D, Srolovitz D J, Rollett A D, Anderson M P.Script Metall, 1987; 21:675 |
[12] | Anderson M P, Grest G S, Doherty R D, Srolovitz D J.Script Metall, 1989; 23:753 |
[13] | Song X Y, Liu G Q, Gu N J. Acta Metall Sin, 1999; 35:565(宋晓艳,刘国权,谷南驹.金属学报,1999;35:565) |
[14] | Rios P R. Acta Metall, 1987; 35:2805 |
[15] | Haroun N A. J Mater Sci, 1980; 15:2816 |
[16] | Hazzledine P M, Oldershaw R D J. Philo Mag, 1990; 61A:579 |
[17] | Syn C K, Lesuer D R, Sherby O D. Metall Mater Trans,1994; 25A: 1481 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%