介绍了获得满足△9平行法则的位向关系、惯习面、正空间和倒空间准不变应变线的计算方法,解释了高锰钢中先共析魏氏组织渗碳体在奥氏体晶内析出时的Pitsch和T-H位向关系.计算得到的位向关系和惯习面结果与实验结果吻合得很好.根据计算结果,将惯习面分解成原子级的台阶,绘制了Pitsch和T-H位向关系惯习面上的晶格匹配示意图.
参考文献
[1] | Thompson S W, Howell P R. Scr Metall, 1987; 21:1353 |
[2] | Thompson S W, Howell P R. In: Johnson W C, Howe J M, Laughlin D E, Soffa W A eds., Proc Int Conf SolidSolid Phase Transformations, Warrendale, Pennsylvania:TMS, 1994:1127 |
[3] | Spanos G, Aaronson H I. Acta Metall Mater, 1990; 38:2721 |
[4] | Yang K H, Choo W K. Acta Metall Mater, 1994; 42:263 |
[5] | Howe J M, Spanos G. Philos Mag, 1999; A79:9 |
[6] | Farooque M, Edmonds D V. In: Peachey L D, Williams D Beds., Proc 12th Int Cong for Electron Microscopy, San Francisco, California: San Francisco Press Incorporated Company, 1990:910 |
[7] | Khalid F A, Edmonds D V. Acta Metall Mater, 1993; 41:3421 |
[8] | Zhang M-X, Kelly P M. Scr Mater, 1997; 37:2017 |
[9] | Zhang M-X, Kelly P M. Acta Mater, 1998; 46:4617 |
[10] | Pitsch W. Acta Metall, 1962; 10:897 |
[11] | Pitsch W. Arch Eisenhuttenwes, 1963; 34:381 |
[12] | Thompson S W, Howell P R. Scr Metall, 1988; 22:229 |
[13] | Zhang W-Z, Purdy G R. Philos Mag, 1993; A68:291 |
[14] | Zhang W-Z. In: Koiwa M , Otsuka K , Miyazaki Teds.,Proc Int Conf Solid-Solid Phase Transformations, Kyoto,Japan: The Japan Institute Metals, 1999:581 |
[15] | Duly D, Zhang W-Z , Audier M. Philos Mag, 1995; A71:187 |
[16] | Xiao S Q, Dahmen U, Maloy S A, Heuer A H. Mater Sci Forum, 1996; 207-209:117 |
[17] | Zhang W-Z, Purdy G R. Acta Metall, 1993; 41:543 |
[18] | Weatherly G C, Zhang W-Z. Metall Mater Trans, 1994;A25:1865 |
[19] | Zhang W-Z, Ye F, Zhang C, Qi Y, Fang H-S. Acta Mater,2000; 48:2209 |
[20] | McClune W F. Powder Diffraction File. JCPDS International Centre for Diffraction Data, No. 35-772, Swarthmore, Pennsylvania, 1989 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%