在室温条件下,球磨Si,C混合粉末合成纳米尺寸SiC.采用高分辨电子显微术在原子尺度上详尽地表征了该反应过程.高分辨像表明,在球磨过程中首先形成非晶C(a-C)、非晶Si(a-Si)以及纳米晶Si(c-Si),为合成SiC提供了适宜条件.SiC的合成主要是通过C原子向a-Si及c-Si的扩散.对于前者,形成非晶a-Si(C),然后机械力诱使非晶a-Si(C)晶化;对于后者,C原子直接取代Si原子形成SiC,具有取向关系(111)siC∥(111)si.在一些区域内,还发生局域自蔓延反应,形成稍大尺寸的SiC晶粒.
参考文献
| [1] | Davis R M, McDermott B, Koch C C. Metall Trans, 1988;19A: 2867 |
| [2] | Koch C C. Annu Rev Mater Sci, 1989; 19:121 |
| [3] | Yang Z G, Shaw L L. Nanostruct Mater, 1996; 7:873 |
| [4] | El-Eskandarany M S, Sumiyama K, Suzuki K. J Mater Res, 1995; 10:659 |
| [5] | Matteazzi P, le Gca(e)r G. J Am Ceram Soc, 1991; 74:1382 |
| [6] | Feng G, Shi L J, Lü J, Lu K. Acta Metall Sin, 2000; 36:300(冯淦,石连捷,吕坚,卢柯.金属学报,2000;36:300) |
| [7] | Atzmon M. Phys Rev Lett, 1990; 64:487 |
| [8] | Narayan J, Raghunatnan R, Chowdhury R, Jagannadham K. J Appl Phys, 1994; 75:7252 |
| [9] | Huang J Y, Yasuda H, Mori H. Philos Mag Lett, 1999; 79:305 |
| [10] | Huang J Y. Acta Mater, 1999; 47:1801 |
| [11] | Inui H, Mori H, Fujita H. Philos Mag, 1990; 61B: 107 |
| [12] | Maurice D R, Courtney T H. Metall Trans, 1990; 21A:289 |
| [13] | Fan G J, Quan M X, Hu Z Q, Li Y L, Liang Y. Appl Phys Lett, 1996; 68:915 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%