经等离子重熔的Al-16Si合金与电阻炉重熔的相比,组织有明显的细化效果:初晶Si最大长度由120 μm变为10μm,共晶Si最大长度由75 μm变为8 μm,并且这种细化效果随着放电电流和气流量的增大而增强.分析认为,造成组织细化的原因是由于等离子熔炼特殊的加热方式所致.等离子轰击作用能使熔体中保留遗传信息的原子团簇变小,微观结构更加均匀.
参考文献
| [1] | Pzcz A Z. US Pat, No.13887900, 1920 |
| [2] | Denton J R, Spittle J A. Mater Sci Technol, 1985; 1:305 |
| [3] | Flemings M C. Metall Trans, 1991; 22B: 269 |
| [4] | Misra A K. Metall Trans, 1985; 16A: 1354 |
| [5] | Maesiar H. Giessereitechnik, 1985; 31(7): 211 |
| [6] | Boening H V. Plasma Science and Technology. London:Cornell University Press, 1982:13 |
| [7] | Oskam H J. Plasma Processing of Materials. USA: Noyes Publications, 1984:244 |
| [8] | Ruset C. Heat Treat Met, 1990; (2): 51 |
| [9] | Sinha O P. Tool Alloy Steels, 1990; (12): 463 |
| [10] | Bian X F, Liu X F, Ma J J. Heredity in Cast Metals.Jinan: Shandong Science and Technology Press, 1999:2(边秀房,刘相法,马家骥.铸造金属遗传学.济南:山东科学技术出版社,1999:2) |
| [11] | Cui Z Q. Metallography and Heat-Treatment. Beijing:Mechnical Industry Press, 1994:41(崔忠圻.金属学与热处理.北京:机械工业出版社,1994:41) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%