采用三维弹塑性大变形热力耦合有限元法,模拟薄板坯连铸液芯铸轧过程中的坯壳变形,分析影响铸坯纵向伸长的主要因素.提出动态反向堆钢理论,对有限元模拟结果和在线热带生产(ISP)工艺中的铸轧技术做出了合理解释.