应用定向凝固技术制备了Cr系白口铸铁,采用萃取法制备碳化物试样,用失重法测得腐蚀速率,并通过电化学法探讨Cr系白口铸铁在腐蚀介质中的相间腐蚀机理.结果表明:(1)Cr系白口铸铁在腐蚀介质中存在严重的相间腐蚀,相间腐蚀失重率占合金总腐蚀失重率的一半以上;(2)碳化物的电化学行为不同于合金和基体,一直处于自钝化状态,M7C3型碳化物比M3C型更耐蚀、更稳定;(3)碳化物与基体两相间的腐蚀电位差是相间腐蚀的驱动力,在此腐蚀过程中,碳化物被保护,基体被加速腐蚀.提高基体的腐蚀电位,不仅可以降低相间腐蚀速率,而且能够大幅度提高Cr系白口铸铁的耐蚀性.
参考文献
| [1] | Gahr K H Z, Eldis G T. Wear, 1980; 64:175 |
| [2] | Parent S, Margerier J C. AFS Trans, 1972; 80:393 |
| [3] | Gundlach R B. AFS Trans, 1974; 82; 309 |
| [4] | Dupin P, Saverna J, Schissler J M. AFS Trans, 1982; 90:711 |
| [5] | Xing J D, Zhou Q D. AFS Trans, 1992; 100:17 |
| [6] | Wu W Z, Xing J D, Su J Y. Acta Metall Sin, 1997; 33:1075(武文忠,邢建东,苏俊义.金属学报,1997;33:1075) |
| [7] | Pitt C H, Chang Y M. Corrosion, 1986; 42:312 |
| [8] | Bronson A, Nelson J, Kang C. Wear, 1992; 154:387 |
| [9] | Zhou Q D. Chromium Anti-Wear Cast Iron. Xi'an: Xi'an Jiaotong University Publishing House, 1987:102(周庆德.铬系抗磨铸铁.西安:西安交通大学出版社,1987:102) |
| [10] | Jiang X X, Wang J Y. Alloy Phase Electrochemistry.Shanghai: Shanghai Science and Technology Publishing House, 1984:90(姜晓霞,王景蕴.合金相电化学.上海:上海科学技术出版社,1984:90) |
| [11] | Zhang A F, Xing J D, Gao Y M, Su J Y. J Xi'an Jiaotong Univ, 2000; 34(7): 36(张安峰,邢建东,高义民,苏俊义.西安交通大学学报,2000;34(7):36) |
| [12] | Zheng Y G, Yao Z M, Li C S, Wang S C, Ke W. J Chin Soc Corros Protect, 1993; 13:390(郑玉贵,姚治铭,李春生,王世才,柯伟.中国腐蚀与防护学报,1993;13:390) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%