金属纳米块体材料具有独特的力学性能,如高强度、超高延展性等,近年来得到了广泛深入的研究.在对其新进展进行简要评述的基础上,讨论了它的强度、塑性、弹性模量、应变强化、超塑性、蠕变及变形机理等相关问题.
参考文献
[1] | Birringer R, Herr U, Gleiter H. Suppl Trans Jpn Inst Metall, 1986; 27:43 |
[2] | Gleiter H. Prog Mater Sci, 1989; 33:223 |
[3] | Hall E O. Proc Phys Soc London, 1951; B64: 747, Petch N J. J Iron Steel Inst, 1953; 174:25 |
[4] | Hall E O. Proc Phys Soc London, 1951; B64: 747, Petch N J. J Iron Steel Inst, 1953; 174:25 |
[5] | Jang J S C, Koch C C. Scr Metall Mater, 1990; 24:1599 |
[6] | Brun P Le, Gaffet E, Froye L, Delay L. Scr Metall Mater,1992; 26:1743 |
[7] | Chokshi A H, Rosen A, Karch J, Gleiter H. Scr Metall Mater, 1989; 23:1679 |
[8] | Lu K, Wei W D, Wang J T. Scr Metall Mater, 1990; 24:2319 |
[9] | Wang J T, Hu Z Q, Ding B Z. Mater Sci Eng, 1993; A169:117 |
[10] | Chang H, Altstetter C J, Averback R S. J Mater Res,1992; 7:2962 |
[11] | Siegel R W, Fougere G E. Nanostr Mater, 1995; 6:205 |
[12] | Nieman G W, Weertman J R, Siegel R W. J Mater Res,1991; 6:1012 |
[13] | Nieh T G, Wadsworth J. Scr Metall Mater, 1991; 25:955 |
[14] | Schiφtz J, Di Tolla F D, Jacobsen K W. Nature, 1998;391:561 |
[15] | Schiφtz J, Vegge T, Di Tolla F D, Jacobsen K W. Phys Rev, 1999; B60:11971 |
[16] | Sanders P G, Eastman J A, Weertman J R. Acta Mater,1997; 45:4019 |
[17] | Lu L, Wang L B, Ding B Z, Lu K. J Mater Res, 2000; 15:270 |
[18] | Youngdahl C J, Sanders P G, Eastman J A. Weertman J R. Scr Mater, 1997; 37:809 |
[19] | Jia D, Ramesh K T, Ma E. Scr Mater, 1999; 42:73 |
[20] | Karch J, Birringer R, Gleiter H. Nature, 1987; 330:556 |
[21] | Bohn R, Haubold T, Birringer R, Gleiter H. Scr Mater,1991; 25:811 |
[22] | Koch C C, Morris D G, Lu K, Inoue A. MRS Bull, 1999;24:54 |
[23] | Sui M L, Patu S, He Y Z. Scr Metall Mater, 1991; 25:1537 |
[24] | Shen T D, Koch C C, Tsui T Y, Pharr G M. J Mater Res,1995; 10:2892 |
[25] | Masumoto T, Maddin R. Mater Sci Eng, 1975; 19:1 |
[26] | Coble R L. J Appl Phys, 1963; 34:1679 |
[27] | McFadden S X, Mishra R S, Valiev R Z, Zhilyaev A P,Mukherjee A K. Nature, 1999; 398:684 |
[28] | Lu L, Sui M L, Lu K. Science, 2000; 287:1463 |
[29] | Wang N, Wang Z R, Aust K T, Erb U. Mater Sci Eng,1997; A237:150 |
[30] | Cai B, Kong Q P, Lu L, Lu K. Scr Mater, 1999; 41:755 |
[31] | Lu K. Mater Sci Eng Rep, 1991; 16:161 |
[32] | Wang D L, Kong Q P, Shui J P. Scr Metall Mater, 1994;31:47 |
[33] | Sanders P G, Rittner M, Kiedaisch E, Weertman J R,Kung H, Lu Y C. Nanostr Mater, 1997; 9:433 |
[34] | Keblinski P, Wolf D, Gleiter H. Interface Sci, 1998; 6:205 |
[35] | Wolf D. Private Communication, 2000 |
[36] | Swygenhoven H Van, Caro A. Appl Phys Lett, 1997; 71:1652 |
[37] | Ke M, Hackney S A, Milligan W W, Aifantis E C. Nanostr Mater, 1995; 5:689 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%