将研究晶态材料弛豫过程中粘度的唯象办法-四参数力学模型法与描述非晶材料的双能级模型统一起来,同时运用激活能谱理论对非晶材料弛豫过程中的粘度进行了唯象研究,得到了新的弛豫规律;并应用此规律对等温弛豫过程中的粘度进行了数值分析,得到了一些有用的结论.
参考文献
[1] | Luborsky F E. Amorphous Metallic Alloys. Butterworth & Co (Publishers) Ltd, 1983:1 |
[2] | Guo Y C, Wang Z X. Amorphous Physics. Beijing: Academic Press, 1984:187 |
[3] | Elliott S R. Physics of Amorphous Materials. New York,1984:30 |
[4] | Spaepen F. Acta Metall, 1977; 25:407 |
[5] | Taub A I, Spaepen F. Acta Metall, 1980; 28:1781 |
[6] | Tsao S S, Spaepen F. In: Proc 4th Int Conf on Rapidly Quenched Metals, Sandai, 1981:463 |
[7] | Tsao S S, Spaepen F. Acta Metall, 1985; 33:881 |
[8] | Ma X M, He Y Z. Acta Metall Sin, 1987; B23:18 |
[9] | Zheng F Q. Acta Phys Sin, 1991; 40:262 |
[10] | Limoge Y, Breblc G. Acta Metall, 1988; 36:665 |
[11] | Anne S, Daniel R, Neuville P R. J Non-Cryst Solids, 1977;211:281 |
[12] | Cai J L, Qiao C L. Chin Phys Lett, 1998; 15:281 |
[13] | Zhou S X. Quantum Mechanics. Beijing: People's Education Press, 1979:49 |
[14] | Ke T S, Zhang L D. Internal Friction & Ultrasonic Attenuation in Sloids. Beijing: Atomic Energy Press, 1989:45 |
[15] | Chen H S. J Appl Phys, 1978; 49:3290 |
[16] | Taub A I, Spaepen F. Scr Metall, 1980; 14:1197 |
[17] | Beukel V D. Acta Metall, 1986; 34:483 |
[18] | Kong Q P, Shan B. Acta Phys Sin, 1989; 38:1299 |
[19] | Hygate G, Gibbs M R J. J Phys F: Met Phys, 1987; 17:815 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%