通过球磨可以极大地细化AlN陶瓷的晶粒尺寸,透射电镜(TEM)观察的结果表明,经过40 h的球磨后,晶粒尺寸由原始的40 μm减小到30-200 nm.高分辨电镜(HREM)观察表明,球磨过程中在大晶粒内形成了高密度的位错和很高的微应变,晶粒细化过程是一个通过位错产生、运动和重排使大晶粒分解为亚晶粒的塑性变形过程.在晶粒细化的同时,在磨球的剧烈作用下,AlN颗粒表面层晶格发生严重畸变,甚至失去其固有结构特征.
参考文献
| [1] | Benjamin J S. Matall Mater, 1970,1:2493 |
| [2] | Fecht H J, Hellstern E, Fu Z, Johnson W L. Metall Trans,1990,21A: 2333 |
| [3] | Iellstern E, Fecht H J, Fu Z, Johbnson W L. J Appl Phys,1989,65:305 |
| [4] | Fecht H J. Nanostruct. Mater, 1995,6:33 |
| [5] | Kimura H, Kimura M, Takada F. J Less-common Metals,1988,140:113 |
| [6] | Yang X Y, Wu Y K, Ye H Q. Philosph Mag Lett, 2000;80:333 |
| [7] | Huang J Y, Yasuda H, Mori H. Philosph Mag Lett, 1999;79:305 |
| [8] | Pezzotti G, Lee B T. Hiraga K. J Mater Sci, 1994,29:1786 |
| [9] | Lee B T, Hiraga K. J Mater Res, 1994,9:1199 |
| [10] | Lee B T, Nishiyama A, Hiraga K. Mater Trans, 1993;JIM34:682 |
| [11] | Edgar J H. J Mater Res, 1992,7:235 |
| [12] | Mroz T J. Ceram Bull, 1992,71:782 |
| [13] | Masson I, Feiereisen J P, Michel J P, Mocellin A, Guenard C. Br. Ceram Trans J, 1992,91:177 |
| [14] | Seifert A, Berger A, Muller W F. J Am Ceram Soc, 1992;75:873 |
| [15] | Audurier V, Demenet J L, Rabier J. Philosph Mag, 1998;A77:825 |
| [16] | Audurier V, Demenet J L, Rabier J. Philosph Mag, 1998;A77:843 |
| [17] | Jiang J S C, Koch C C. J Mater Res, 1990,5:498 |
| [18] | Schwarz R B, Johnson W L. J Less-Common Met, 1988;140: 1 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%