通过研究相同过热度下Al-Si合金熔体中的氢含量,发现氢含量曲线具有和液相线类似的变化规律,即随着Si含量的增加,试样中的氢含量先减少,到共晶点时为最小此后氢含量又逐渐增加.并且过热度越大,氢含量越高合金液态结构X射线衍射结果表明,熔体中原子密度随着Si含量的变化趋势与氢含量曲线相反用熔体"自由体积理论”解释了铝熔体氢含量的变化规律.
参考文献
| [1] | Prince N. Anyalebechi. Scrip Metall Mater, 1995,33:1209 |
| [2] | Kang J X, Fu G S. Special Casting Nonferrous Alloys,1995,5:5(康积性,傅高升.特种铸造及有色金属,1995;5:5) |
| [3] | Teixwira J. Mater Sci Eng, 1994,178A: 9 |
| [4] | Wang W M. Ph D Thesis, Shandong University of Technology, Jinan, 1998(王伟民.山东工业大学博士学位论文,济南,1998) |
| [5] | Prishnova A G, Mazur V I, Taran Yu N, Rostovskaya L A, Persion Z V, Hristenko T M, Rimanova A V. Metall,1983,5:88(пp иши o в a Aг, Ma э y p Bи, Ta pa нЮН,р o c товск a ялA, пe p c и o и 3 B, Xp и cт e нк o TM, р o Ma нов a AB. Me т a лл o Физик a , 1983,5: 88) |
| [6] | Prishnova A G, Mazur V I, Taran Yu N, Rostovskaya L A, Persion Z V, Hristenko T M, Rimanova A V. Metall,1983,5:54(пpищнов a Aг, Ma з y p Bи, Tap a нЮН,рo c товск a ялA, пe p c и oн 3 B, Xpиcт e нк o TM, рo мa н o в a AB. Me т a ллоФизик a , 1983;5: 54) |
| [7] | Eyring H. J Chem Phys, 1936,4:241 |
| [8] | Doolittle A K. J Appl Phys, 1951,22:1031 |
| [9] | Zhang Z X. Common Datasheet of Physics. Beijing: Science Press, 1981:107(张质贤物理学常用数表,北京:科学出版社,1981:107) |
| [10] | Zhang Z H, Bian X F. Acta Metall Sin, 2000,36:33(张忠华,边秀房金属学报,2000;36:33) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%