埋地管道在近中性pH和高pH环境中的应力腐蚀开裂

金属学报, 2001, 37(5): 453-458. doi: 10.3321/j.issn:0412-1961.2001.05.002

埋地管道在近中性pH和高pH环境中的应力腐蚀开裂

方丙炎 ^1, , 王俭秋 ^2, , 朱自勇 ^3, , 韩恩厚 ^4, , 柯伟 ^5,

1.中国科学院金属研究所金属腐蚀与防护国家重点实验室,沈阳,110016

2.中国科学院金属研究所金属腐蚀与防护国家重点实验室,沈阳,110016

3.中国科学院金属研究所金属腐蚀与防护国家重点实验室,沈阳,110016

4.中国科学院金属研究所金属腐蚀与防护国家重点实验室,沈阳,110016

5.中国科学院金属研究所金属腐蚀与防护国家重点实验室,沈阳,110016

基金项目: 中国科学院"百人计划"(G19990650)

关键词：管线钢 , 应力腐蚀 , 开裂 , 阳极溶解 , 氢脆

THE STRESS CORROSION CRACKING OF BURIED PIPELINES IN NEAR-NEUTRAL-pH AND HIGH-pH SOLUTIONS

综述了埋地管道经典型的高pH应力腐蚀开裂(高pH SCC)与近十多年来发现和研究的近中性pH应力腐蚀开裂(近中性pH SCC)的异同,影响因素以及机理,最后展望了埋地管道的未来研究方向.

参考文献

[1]	Townsend Jr H E. Mater Performance, 1972,11:33
[2]	Wenk R L. In: American Gas Association ed, 5th Symp on Line Pipe Reseach, Arlington: American Gas Association Inc, 1974:T-1
[3]	Kentish P J. Brit Corros J, 1985,20:139
[4]	Delanty B, O'Beirne J. Oil Gas J, 1992,90(24): 39
[5]	Parkins R N. In: National Associationo of Corrosion Engineers ed, Research Topical Symp, Houston: National Associationo of Corrosion Engineers, 1996:1
[6]	Sutcliffe J M, Fessler R R, Boyd W K, Parkins R N. Corros, 1972,28:313
[7]	Parkins R N, Greenwell B S. Met Sci, 1977,11:405
[8]	Fessler R R. In: American Gas Association ed, 6th Symp on Line Pipe Research,Arlington: American Gas Association Inc, 1979:R-1
[9]	Barlo T J. In: American Gas Association ed, 6th Symp on Line Pipe Research , Arlington: American Gas Association Inc, 1979:U-1
[10]	Beavers J A, Parkins R N. In: American Gas Association ed, 7th Symp on Line Pipe Research, Arlington: AmericanGas Association Inc, 1986:P25-1
[11]	Beavers J A, Berry W E, Parkins R N. Mater Performance, 1986,25:9
[12]	Beavers J A. Christman T K, Parkins R N. Mater Perfor-mance, 1988,27:22
[13]	Parkins R N. Corrosion, 1990,46:178
[14]	Parkins R N, Markworth A J, Holbrook J H. Corrosion,1988,44:572
[15]	Parkins R N, Singh P M. Corrosion, 1990,46:485
[16]	Christman T K. Corrosion, 1990,46:450
[17]	Parkins R N, Belhimer E, Blanchard Jr W K . Corrosion,1993,49:951
[18]	Delanty B, O'Beirne J. Oil Gas J, 1985,85(20): 139
[19]	Justice R H, Mackenzie J D. In: American Gas Association ed, Proc NG-19 /EPRG 7th Biennial Joint Technical Meeting on Line Pipe Research, Pipeline Research Committee of the American Gas Association, Arlington, 1988:28
[20]	Parkins R N, Blanchard W K, Delanty B S. Corrosion,1994,50:394
[21]	Szklarska-Smialowska Z, Xia Z, Rebak R B. Corrosion,1994,50:334
[22]	Harle B A, Beavers J A. Corrosion, 1993,49:861
[23]	Plumtee A, Lambert S B. In: American Society of Mechanical Engineers ed, Int Pipeline Conf, Vol.1, New York: American Society of Mechanical Engineers, 1996:565
[24]	Ahmed T M, Lambet S B, Sutherby R, Plumtree A. Corrosion, 1998,54:115
[25]	Nielsen L V. In: Jackman P S, Smith L M eds, European Federation of Corrosion Publications, Paper No.11, Nice, France: Institute of Materials, 1999:11
[26]	Parkins R N, Fesser R R. Mater Eng Appl, 1978,1:80
[27]	Zheng W, Macleod F A, Revie R W, Tyson W R, Shen G, Kiff D, Skaff M. Wong E-W. In: Jackman P S, Smith L M eds, Institute of Material Communications, European Federation of Corrosion Publications, 1996:28
[28]	Wilmott M J, Diakow D A. In: American Society of Mechanical Engineer ed, Proc 1st Int Pipeline Conf, IPC/96, New York: American Society of Mechanical Engineers,1996:574
[29]	Krishnamurthy R M, MacDonald R W, Marreck P M. In:American Society of Mechanical Engineer ed, Proc 1st Int Pipeline Conf, IPC/96, New York: American Society of Mechanical Engineers, 1996:495
[30]	Wilmott M J, Jack T R, Van Boven G. In: National Association of Corrossion Engineers ed, Corrosion 96, Paper No.242, Houston: National Association of Corrossion Engineers, 1996:242
[31]	National Association of Crossion Engineers. NACE Standard RPO169-92. Houston: NACE, 1992:13
[32]	Parkins R N, Markworth A J, Holbrook J H. Corrosion,1987,43:572
[33]	Parkins R N. In: American Gas Association ed, 5th Symp on Line Pipe Research, Arlington: American Gas Association Inc, 1974:U-1
[34]	Feiman L I, Yunovich M Y. Prot Met, t986,24:78
[35]	Feiman L I, Yunovich M Y. Prot Met, 1991,29:354
[36]	Beavers J A, Thompson N G. Unpublished Research Performed at Cortest Columbus Technologies for Trans Canada Pipelines Limited, Ohio University, Ohio, 1988
[37]	Barth C F. Ph D Thesis, Case Western Rreseerve University, America, 1971
[38]	Hirth J P. In: Gibala R, Hehemam R Feds, Theories of Hydrogen-Induced Cracking of Steel in Hydrogen Embrittlement Metals Pork, OH, ASM, 1980:29
[39]	Barlo T J. In: American Gas Association ed, 6th Symp on Line Pipe Research, Arlington: American Gas Association Inc, 1979:P-1
[40]	Beavers J A , Harle B A. In: American Society of Mechanical Engineer ed, Proc 1st Int Pipeline Conf, IPC/96, New York: American Society of Mechanical Engineers, 1996:573
[41]	Szklarska Smialowska Z. In: Chan S L I, Tsai W Teds, Corrosion Prevention for Industrial Safety and Environmental Control, Taiwan, 1995:31
[42]	Beavers J A, Christman T K, Parkins R N. Corros/87,1987:178
[43]	Harle B A, Beavers J A, Jaske C C. In: National Association of Corrossion Engineers ed, Corrosion/95, Houston: National Association of Corrossion Engineers, 1995:646
[44]	Serebrinsky S A, Duff G S, Galvele J R. Corros Sci, 1999,41:191
[45]	Parkins R N. J Iron Steel Inst, 1952,172:149
[46]	Parkins R N. In: American Gas Association ed, 1st Sympo on Line Pipe Research, Arlington: American Gas Association Inc, 1974:174
[47]	Wang J Q, Atrens A, Cousens D R, Nockolds C, BulcockS. J Mater Sci, 1999,34:1711
[48]	Wang J Q, Atrens A, Cousens D R, Kinaev N. J Mater Sci, 1999,34:1721
[49]	Wang J Q, Atrens A, Cousens D R, Nockolds C, BulcockS. Acta Metall, 1998,46:5677
[50]	Cousens D R, Wood B J, Wang J Q, Atrens A. Surf Interface Anal, 2000,29:23
[51]	Parkins R N, Delanty B S. In: National Association of Corrossion Engineers ed, National Association of Corrossion Engineers Fall Committee Week, Sept.26-Oct.1, Houston: National Association of Corrossion Engineers,1993:16
[52]	Rebak R B, Xia Z, Safruddin R, Szklarsla-Smialowska Z. Corrosion, 1996,52:396
[53]	Harle B A, Beavers J A, Jaske C E. Corros/94, 1994:242
[54]	Harle B A, Beavers J A, Jaske C E. Corros/95, 1995:646
[55]	Plumtree A, Lambert S B, Sutherby R. In: Magnin T ed, European Federation of Corrosion Publications,Nice, France, Paper No.26, Institute of Materials, 1997: 26
[56]	Qiao L J, Luo J L, Mao X. Corrosion, 1998,54:115
[57]	Schmidt G. Corros/83, 1983:3
[58]	Gu B, Yu W Z, Luo J L, Mao X. Corrosion, 1999,55:312
[59]	Gu B, Luo J, Mao X. Corrosion, 1999,55:96
[60]	Wang Z F, Atrens A. Metall Mater Trans, 1996,27A: 2686

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

埋地管道在近中性pH和高pH环境中的应力腐蚀开裂

THE STRESS CORROSION CRACKING OF BURIED PIPELINES IN NEAR-NEUTRAL-pH AND HIGH-pH SOLUTIONS

参考文献