采用硼(B)径迹照相法和透射电镜从实验上观察了连续冷却过程中B在晶界非平衡偏聚的发生发展过程,测定了晶界偏聚的富集因子、富集带宽度、贫B区宽度和贫化因子等偏聚特征参量.实验结果表明,对于B含量(质量分数)为10×10-4%的Fe-40%Ni合金体系,以2℃/s的冷速从1150℃冷却到640℃的时候,B在晶界上的偏聚经历了3段式的发展,并在860℃时开始向非平衡析出转化.可以用晶界及晶界附近扩展畸变区对于溶质原子的吸附作用解释上述现象.
参考文献
| [1] | He X L, Chu Y Y, Zhang X L, Yu Z S. Acta Metall Sin,1977; 13:235(贺信莱,褚幼义,张秀林,余宗森,金属学报,1977;13:235) |
| [2] | Karlsson L, Norden H, Odelius H. Acta Metall, 1988; 36:1 |
| [3] | Vorlicek V, Flewitt P E. Acta Metall Mater, 1994; 42:3309 |
| [4] | Misra R D K, Rao P R. Mater Sci Technol, 1997; 13:277 |
| [5] | Letellier L, Guttmann M, Blavette D. Philos Mag Lett,1994; 70:189 |
| [6] | Faulkner R G. J Mater Sci, 1981; 16:373 |
| [7] | Xu T D. J Mater Sci, 1987; 22:337 |
| [8] | HeXL, Chu Y Y. J Phys D:Appl Phys, 1983; 16:1145 |
| [9] | Chapman M A V, Faulkner R G. Acta Metall, 1983; 31:677 |
| [10] | Karlsson L. Acta Metall, 1988; 36:25 |
| [11] | Zhang S H, He X L, Ko T. J Mater Sci, 1994; 29; 2663 |
| [12] | Jiang H, Faulkner R G. Acta Mater, 1996; 44:1857 |
| [13] | Carinci G M. Appl Surf Sci, 1994; 76/77:266 |
| [14] | Valiev R Z, Korznikov A V, Mulynkov R R. Mater Sci Eng, 1993; 168 A: 141 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%