通过等温压缩试验和金相分析研究了热变形参数对Ti-15-3(Ti-15V-3Cr-3Sn-3Al)合金固溶处理后显微组织的影响等效晶粒尺寸随变形温度升高而增大.随变形程度和变形速率增加而减小:再结晶程度随变形温度升高而减小.随变形程度和变形速率增加而增大采用人工神经网络的方法建立了等效晶粒尺寸及再结晶晶粒体积百分数与变形程度、变形速率和变形温度间的数学模型.预测值与实测值吻合较好,表明该方法很好地预测热变形参数对Ti-15-3合金固溶处理后显微组织的影响.
参考文献
| [1] | Chen Y W . Chin J Rare Met, 1996; 4:297(陈玉文.稀有金属.1996;4:297) |
| [2] | E.O.Ezugwu, Z M Wang. J Mater Proc Technol, 1997;68:262 |
| [3] | Gottstein G, Marx V, Sebald R . Shanghai Jiaotong Univ, 2000; 5(1): 49 |
| [4] | Zhe W, Takashi I, Nobuki Y, Akira K . Annals CIRP,1999; 48(1): 187 |
| [5] | Yao Z K, Guo H Z, Shu Z W . Rare Met Mater Eng,2000; 29:340(姚泽坤.郭鸿镇.苏祖武.稀有金属材料与工程.2000;29:340) |
| [6] | Cui F K, Wang X Q, Zhang F S . Mater Sci Technol,2000; 8(3): 109(崔凤奎.王晓强.张丰收.材料科学与工艺.2000;8(3):109) |
| [7] | ZhangJ M, GaoZY, ZhuangJY, ZhongZY. JMater Proc Technol, 1999; 88:244 |
| [8] | Xu Y R, Chen LS, Wang D Y. Iron Steel, 2000; 35(10):51(徐有容,陈良生,王德英.钢铁.2000;35(10):51) |
| [9] | Rao K P, Prasad Y K D V. J Mater Proc Technol, 1995;53:552 |
| [10] | Liu Q B, Ji Z, Liu M B . J Mater Proc Technol, 1996;62:206 |
| [11] | Wang X Y, Qiu G Z . Trans Nonferrous Met Soc Chin,1998; 8(1): 142 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%