采用近液相线半连续铸造法制备铸造A356铝合金,获得金属半固态加工要求的细小、等轴的"非枝晶"组织,研究了铸造温度、保温时间及冷却速度对该组织的影响规律结果表明,在液相线附近,降低铸造温度,有利于减小晶粒尺寸;晶粒平均等积圆直径最小可达42.6μm,初始固相体积分数最多可达98.4%.同一温度下,晶粒尺寸随保温时间的延长而粗化;冷却速度快,晶粒尺寸细小;同一铸锭,其中心部位的组织比边缘部位的组织粗大,且分布均匀、等轴特征明显.
参考文献
| [1] | Fleming M C. Metall Tans, 1991; 22B: 269 |
| [2] | Kenney M P, Courtois J A, Evans R D. Metals Handbook.Vol.15, 9th ed., Metals Park, Ohio: ASM, 1988:327 |
| [3] | Kiuchi M, Sugiyama S. J Mater Shaping Technol, 1990;8:39 |
| [4] | Chiarmetta G. In: Kirkwood D H, Kapranos P eds., Proc 4th Int Conf on Semi-Solid Processing of Alloy and Composites. Sheffield: The University of Sheffield, 1996:204 |
| [5] | Nakada M, Shiohara Y, Flemings M C. ISIJ Int, 1990;30(1): 27 |
| [6] | Lu G M, Cui J Z, Dong J, Xia K. Conference Semi-Solid Processing of Alloys and Composites, Iurin, Italy, Sept.,2000:373 |
| [7] | Cui J Z, Lu G M, Liu D, Dong J. J Harbin Inst Technol,2000; 32(4): 110(崔建忠,路贵民,刘丹,董杰.哈尔滨工业大学学报,2000;32(4):110) |
| [8] | Lu G M, Dong J, Cui J Z. Chin J Nonferrous Met, 2001;11:211(路贵民,董杰,崔建忠.中国有色金属学报,2001;11:211) |
| [9] | Chen C P, Tsao C Y A. J Mater Sci, 1995; 30:4019 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%