对单一先驱体、先驱体/惰性填料、先驱体/活性填料体系裂解陶瓷的尺寸变化进行了模型分析.从理论上分析了活性填料体积分数与裂解陶瓷体积收缩率和线收缩率之间的关系.揭示了活性填料的临界体积分数与活性填料反应的产率、反应前后的密度比之间的相关性.以聚碳硅烷先驱体为例.预测了在不同反应情况下,常见活性填料的临界体积分数.增加活性填料体积分数,可降低陶瓷产物的体积收缩率和气孔率.
参考文献
| [1] | Seyferth D. In: Auner N ed., Organosilicon Chemistry:From Molecular to Materials, Weinheim: Verlagsgesel-lechaft, 1994:269 |
| [2] | Seyferth D. Preceramic Polymers: Past, Present, and Future. AD-A 258 327, 1992 |
| [3] | Seyferth D, Nathan B, David P P. J Am Ceram Soc, 1991;74:2687 |
| [4] | Xie Z F, Chen Z H, Xiao J Y. Polym Mater Sci Eng, 2000;16(6): 7(谢征芳.陈朝辉.肖加余.高分子材料科学与工程,2000;16(6):7) |
| [5] | Seyferth D, Heinrich L, Christine A S. J Inorg Organomet Polym, 1992; 2(1): 59 |
| [6] | Greil P. Ceramic Forum Int Ber Dtsh Keram Ges, 1994;71(6): 304 |
| [7] | Greil P, Seibold M. J Mater Sci, 1992; 27:1053 |
| [8] | Zhou C J, Wei H, Chen Z H. Aerosp Mater Technol, 2000;30(4): 8(周长江.魏红,陈朝辉.宇航材料工艺,2000;30(4):8) |
| [9] | Xie Z F, Chen Z H, Li Y Q. J Inorg Mater, 2000; 15:200(谢征芳.陈朝辉.李永清.无机材料学报,2000;15:200) |
| [10] | Xie Z F. PhD Thesis, National University of Defense Technology, Changsha, 2001(谢征芳.国防科学技术大学博士学位论文,长沙,2001) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%