本文研究了Ni-30Al-5Mo-0.5Hf金属间化合物的显微组织及其超塑性变形行为.该合金是由NiAl/Ni3Al/Mo三相组成,在NiAl中分散着大量的条状Ni3Al.在1050-1100℃,应变速率为5.2×10-4-6.24×10-3s-1拉伸变形时,合金呈现超塑性行为;1050℃,5.2×10-4s-1时的最大延伸率达160%,此时对应的应变速率敏感指数为0.46.超塑性变形的机理主要是由于变形过程中的动态回复和再结晶,同时合金中的NiAl和Ni3Al两相在高温下可以协调变形.
参考文献
| [1] | Oikawa M, Hanada S, Sakai T, Watanabe S. Mater Trans JIM, 1995; 36:1140 |
| [2] | Kim W Y, Hanada S, Takasugi T. Scr Mater, 1997; 37:1053 |
| [3] | Lin D Q, Shan A D, Liu Y, Lin T L. Scr Mater, 1995; 33:681 |
| [4] | Fujino S Karoishgi N, Yoshino M, Mukai T, Okanda Y,Higashi K. Scr Mater, 1997; 37:673 |
| [5] | Chen R S, Guo J T, Yin W M, Zhou J Y. Scr Mater, 1999;40:209 |
| [6] | Takasugi T, Kishino J, Hanada S. Acta Metal Mater, 1993;41:1009 |
| [7] | Qi Y H, Guo J T, Cui C Y. Chin J Nonferrous Met, 2002;12:245(齐义辉,郭建亭,崔传勇中国有色金属学报,2002;12:245) |
| [8] | Misra A, Gibala R and Noebe R D. Metall Mater Trans,1999; 30A: 1003 |
| [9] | Guo J T, Cui C Y, Chen Y X, Li D X, Ye H Q. Internet,2001; 9:287 |
| [10] | Zhou W L, Guo J T, Chen R S, Zhou J Y. Acta Metali Sin, 1999; 35:995(周文龙,郭建亭,陈容石,周继扬.金属学报,1999;35:995) |
| [11] | Lin D L, Li D Q, Liu Y. Intemet, 1998; 6:243 |
| [12] | Gao D C,Yang W Y, Huang C X, Sun Z Q. Acta Metali Sin, 2001; 37:291(高德春,杨王玥,黄春旭,孙祖庆.金属学报,2001;37:291) |
| [13] | Noebe R D, Cullers C L. J Mater Res, 1992; 7:604 |
| [14] | Nieh T G. Mater Res Soc Symp Proc, 1990; 189:196 |
| [15] | Liu Z Y, Lin T L, Gu Y F, Cao P, Lei C M, Huang B Y.Acta Metall Sin, 1996; 32:1139(刘震云,林栋梁,谷月峰,曹鹏,雷长明,黄伯云.金属学报,1996;32:1139) |
| [16] | Cui C Y, Chen Y X, Guo J T, Qi Y H, Ye H Q. Mater Sci Eng A, 2002; 325A: 187 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%