对晶粒组元因晶体生长时沿晶界发生旋转的铜双晶体进行了恒定塑性应变幅下的循环形变研究,塑性应变幅为1.5×10-3.通过扫描电子显微镜-电子通道衬度技术(SEM-ECC)对滑移形貌和位错组态的演化进行了观察,发现由于晶粒内部的几何效应使沿晶界的位错组态随着晶粒的旋转方向的变化也相应发生变化,逐渐表现为由滑移带与晶界的相互作用过渡到形变带与晶界的相互作用.形变带Ⅱ(DBⅡ)对于主滑移有着明显的阻碍作用.晶界无位错区(DFZ)伴随着形变带Ⅱ在晶界的出现而产生.胞状结构的形成是由于次滑移系的开动使形变带Ⅱ中的位错墙结构先破坏而后形成.
参考文献
[1] | Kuhlmann-Wilsdof D, Laird C. Mater Sci Eng, 1977; 27:137 |
[2] | Jin N Y, Winter A T. Acta Metall, 1984; 32:989 |
[3] | Laid C, Buchinger L. Metall Trans, 1985; 16A: 2201 |
[4] | Lisiecki L L, Weertman J R. Acta Metall Mater, 1990; 38:509 |
[5] | Basinski Z S, Korbel A S, Basinski S J. Acta Metall, 1980;28:191 |
[6] | Mughrubi H. In: Loretto M H ed., Dilocation and Properties of Real Materials, London: The Institute of Metals,1985:244 |
[7] | Hunsche A, Neumann P. Acta Metall, 1986; 34:207 |
[8] | Ma B T, Laird C. Acta Metall, 1989; 37:325 |
[9] | Ma B T, Laird C. Acta Metall, 1989; 37:337 |
[10] | Li S X, Li Y, Li G Y, Wang Z G, Lu K. Philos Mag, 2002;82A: 867 |
[11] | Winter A T, Pedersen O B, Rasmussen K V. Acta Metall,1981; 29:735 |
[12] | Wang Z R, Laird C. Mater Sci Eng, 1988; 100:57 |
[13] | Louh T, Chang C P. Acta Mater, 1996; 44:2683 |
[14] | Wu X J. Adv Mech, 1989; 19:433(吴希俊.力学进展,1989;19:433)Wu X J. Adv Mech, 1990; 20:159(吴希俊.力学进展,1990;20:159) |
[15] | Hirth J P. Metall Trans, 1972; 3A: 3047 |
[16] | Zhou Z Q. Mater Sci Progr, 1989; 3: 1(周自强.材料科学进展,1989;3:1) |
[17] | Shen Z, Wagoner R H, Clark W A T. Acta Metall, 1988;36:3231 |
[18] | Shen Z, Wagoner R H, Clark W A T. Scr Metall, 1986;20:921 |
[19] | Lim L C, Raj R. Acta Metall, 1985; 33:2205 |
[20] | Li Q S, Bretheau T. Acta Metal Sin, 1990; 26:209(李庆生,Bretheau T.金属学报,1990;26:209) |
[21] | Wu J S, Lin D L. Acta Metall Sin, 1996; 32:527(吴建生,林栋梁.金属学报,1996;32:527) |
[22] | Hu Y M, Wang Z G, Li G Y. Scr Mater, 1996; 34:331 |
[23] | Tan X L, Gu H C, Wang Z G. Mater Sci Eng, 1995; 196A:45 |
[24] | Li X W, Wang Z G, Li S X. Philos Mag, 2000; 80A: 8,1901 |
[25] | Reid C N. Deformation Geometry for Materials Scientists. New York: Pergamon Press, 1973:125 |
[26] | Li S X, Li X W, Zhang Z F, Wang Z G. Philos Mag, in press |
[27] | Ackermann F, Kubin L P, Lepinoux J, Mughrabi H. Acta Metall, 1984; 32:715 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%