采用过冷奥氏体在A3-Ar3之间变形工艺,获得平均晶粒尺寸约为2μm的微细铁素体晶粒组织.过冷奥氏体形变过程的组织演变包括两个阶段:形变前期以形变强化相变铁素体转变为主导;当相变基本完成后,形变后期以铁素体的动态再结晶为主.形变强化相变是一以形核为主的过程,是晶粒细化的主要原因.应变量较小时,铁素体主要沿原奥氏体晶界及晶内变形带等位置形核,随应变量的增加,以铁素体转变前沿畸变区的反复形核为主.
参考文献
| [1] | Tamura I, Sekine H, Tanaka T, Ouchi C. Thermomechanical Processing of High Strength Low Alloy Steels. London:Butterworth, 1988:6 |
| [2] | Lewis J, Jonas J J, Mintz B. ISIJ Int, 1998; 38:300 |
| [3] | Beynon J H, Gloss R, Hodgson P D. Mater Forum, 1992;16:37 |
| [4] | Pristner R, Ali L. Mater Sci Technol, 1993; 9:135 |
| [5] | Priestner R, Rios E de los. Met Technol, 1980; 7:309 |
| [6] | Pandi R, Yue S. ISIJ Int, 1994; 34:270 |
| [7] | Hodgson P D, Hickson M R, Gibbs R K. Scr Mater,1999;40:1179 |
| [8] | Hurley P J, Kelly G L, Hodgson P D. Mater Sci Technol,2000, 16:1273 |
| [9] | Mintz B, Jonas J J. Mater Sci Technol, 1994; 10:721 |
| [10] | Mintz B, Lewis J, Jonas J J. Mater Sci Technol, 1997; 13:379 |
| [11] | Priestner R, Hodgson P D. Mater Sci Technol, 1992; 8:849 |
| [12] | Yang W Y, Hu A M, Qi J J, Sun Z Q. Chin J Mater Res,2001; 15:171(杨王玥,胡安民,齐俊杰,孙祖庆.材料研究学报,2001;15: 171) |
| [13] | Sun Z Q, Yang W Y, Qi J J, Hu A M. Mater Sci Eng,accepted |
| [14] | Sunghak L Dongil K, Young K L, Ohjoon K. Metall Mater Trans, 1995; 26A: 1093 |
| [15] | Hurley P J, Muddle B C, Hodgson P D. Mater Sci Technol, 2000; 16:1376 |
| [16] | Hurley P J, HodgsonP D. Mater Sci Eng, 2001; 302:206 |
| [17] | Qi J J, Yang W Y, Sun Z Q. Acta Metall Sin, 2002; 38:629(齐俊杰，杨王玥，孙祖庆.金属学报，2002；38：629) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%