研究了K40S钴基高温合金在700℃和900℃温度条件下由应变控制的高温低周疲劳行为,对疲劳断口形貌进行观察,结果表明:在高温低周疲劳加载条件下,K40S合金疲劳裂纹萌生机制为表面滑移带开裂与表面碳化物相界面开裂的综合作用;疲劳裂纹萌生与扩展方式为穿晶型,瞬断区呈现枝晶断裂特征;碳化物可作为障碍,阻碍疲劳裂纹的扩展,且为主要的二次裂纹策源地;K40S合金高温低周疲劳断裂为机械疲劳与高温环境氧化共同作用的结果.
参考文献
| [1] | Sims C T. J Met, 1969; 21:27 |
| [2] | Sims C T, Hagel W C. The Superalloys, New York: John Wiley & Sons Inc., 1972:145 |
| [3] | Yuan F H. Report of Postdoctoral Work, Institute of Metal Research, The Chinese Academy of Sciences, 1999:27(袁福河.中国科学院,金属研究所博士后工作报告,1999:27) |
| [4] | Alloy Digest, Filling Code Co-10 Cobalt Alloy, UpperMontclair, New Jersey: Engineering Alloys Digest Inc., December 1956 |
| [5] | Yang F M, Sun X F, Zhang W, Kang Y P, Guan H R, HuZ Q. Mater Lett, 2001; 49:160 |
| [6] | Yang F M, Sun X F, Kang Y P, Guan H R, Hu Z Q. Acta Metall Sin, 2001; 37:253(杨富民,孙晓峰,康煜平,管恒荣,胡壮麒.金属学报,2001;37:253) |
| [7] | Remy L, Reuchet J. Mater Sci Eng, 1983; 58:19 |
| [8] | Jiang W H, Yao X D, Guan H R, Hu Z Q. Acta Metall Sin, 1999; 35(S2: 207(姜文辉,姚向东,管恒荣,胡壮麒.金属学报,1999;35(增刊2:207) |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%